Lupoy? HI5002A is a general purpose polycarbonate and acrylonitrile butadiene styrene (PC/ ABS) alloy by LG Chem. Exhibits high performance, high flow and high impact resistance. Lupoy? HI5002A is suitable for processing by injection molding. Used in electric and electronic housings. Complies with UL 94 HB flame rating, GM GMW15581P-ABS PC-T1 and IMDS ID 5712576.

Physical Properties	Metric	English	Comments
Specific Gravity	1.11g/cc	1.11g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0050-0.0080cm/cm @Thickness 3.20 mm	0.0050-0.0080in/in @Thickness 0.126 in	ASTM D955
Melt Flow	8.0g/10 min @Load 2.16 kg, Temperature 250 ?°C	8.0g/10 min @Load 4.76 lb, Temperature 482 ?°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	54.9MPa @Thickness 3.20 mm	7970psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	70 % @Thickness 3.20 mm	70 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	84.3MPa @Thickness 3.20 mm	12200psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	2.06GPa @Thickness 3.20 mm	299ksi @Thickness 0.126 in	10mm/min; ASTM D790
Izod Impact, Notched	=5.59J/cm @Thickness 3.20 mm, Temperature 23.0 ?°C	=10.5ft-lb/in @Thickness 0.126 in, Temperature 73.4 ?°F	ASTM D256

PC/ABS LUPOY HI5002A

简介

ABS工程塑料即PC ABS（工程塑料合金），在化工业的中文名字叫塑料合金，之所以命名为PC ABS，是因为这种材料既具有PC树脂的优良耐热耐候性、尺寸稳定性和耐冲击性能，又具有ABS树脂优良的加工流动性。所以应用在薄壁及复杂形状制品，能保持其优异的性能，以及保持塑料与一种酯组成的材料的成型性。ABS工程塑料最大的缺点就是质量重、导热性能欠佳。它的成型温度取于它们两者原料的之间温度，就是240-265度，温度太高ABS会分解，太低PC料的流动性不良。

PC/ABS应用

1.汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件

2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器

3.电信，移动电话外壳，附件以及智能卡（SIM卡）：

4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道

5.家用电器，如洗衣机，吹风机，微波炉内外部件

PC/ABS注塑模工艺条件:

干燥处理：加工前的干燥处理是必须的。湿度应小于0.04%，建议干燥条件为90~110C，2~4小时。

熔化温度： 230~300C。

模具温度：50~100C。

注射压力：取决于塑件。

注射速度：尽可能地高。