江苏普及塑料有限公司
| 牌号简介About |
|---|
| UNITHENE? LH506是一种高密度聚乙烯（HDPE）开发的注塑应用。UNITHENE? LH506具有优异的冲击强度和增强的抗环境应力，特别适用于体育用品和工业外壳的成型。UNITHENE? LH506可以通过将颜料干混或挤压均匀化到树脂中，很容易着色成任何颜色。 UNITHENE LH506 is a high density polyethylene (HDPE) developed for injection molding applications. Possessing outstanding impact strength and improved resistance to environmental stress, UNITHENE LH506 is specially suitable for molding sport utensils and industrial cases. UNITHENE LH506 could be easily pigmented to any color by either dry blending or extrusion homogenization of pigment into the resin. |
产品描述Product Description
厂家：台湾台聚USI Corporation
类别：HDPEHDPE
用途：工业应用;体育用品;装货箱;
加工条件：注射成型Injection Molding
性能特点：高密度; 冲击性能好; 抗应力开裂;High impact resistance,High density,High ESCR
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 0.955 | g/cm3 | ASTM D792 |
| 熔体质量流动速率Melt Mass-Flow Rate (MFR) | 5.5 | g/10min | ASTM D1238 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | 88 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 脆化温度Brittleness Temperature | -76.0 | ℃ | ASTM D746 |
| 维卡软化温度Vicat Softening Temperature | 125 | ℃ | ASTM D1525 |
| 熔融峰值温度Peak Melting Temperature | 132 | ℃ | ASTM D3418 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 邵氏硬度邵氏硬度 | |||
| 邵氏 D邵氏 D | 68 | ASTM D2240 | |
| 拉伸模量拉伸模量 | |||
| 1% 正割，模压成型1% 正割，模压成型 | 824 | MPa | ASTM D638 |
| 拉伸强度Tensile Strength | ASTM D638 | ||
| 屈服Yield | 24.5 | MPa | ASTM D638 |
| 断裂Break | 28.4 | MPa | ASTM D638 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 760 | % | ASTM D638 |
| 弯曲模量Apparent Bending Modulus | |||
| 23℃ | 902 | MPa | ASTM D747 |