牌号简介About |
---|
Fortron? 1140L6是Fortron 1140L4的更简单的流式版本。它提供了与1140L4基本相同的特性。特别适用于流动长度较长的薄壁零件。这种级别的应用包括泵和电子设备的组件。 Fortron 1140L6 is an easier flow version of Fortron 1140L4. It offers essentially the same characteristics of 1140L4. Especially used for thin walled parts with long flow lengths. Applications made of this grade include components for pumps and electronics. |
产品描述Product Description
厂家:美国塞拉尼斯Celanese EVA Performance Polymers
类别:PPSPPS
用途:泵件;电气/电子应用领域;薄壁部件;
性能特点:防火阻燃等级V-0; 易流动;Good liquidity,V-0
填料:玻璃纤维 40
技术参数Technical Data | |||
---|---|---|---|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179/1eA | ||
-30℃-30°C | 10 | kJ/m2 | ISO 179/1eA |
23℃23°C | 10 | kJ/m2 | ISO 179/1eA |
简支梁无缺口冲击强度Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-30℃-30°C | 53 | kJ/m2 | ISO 179/1eU |
23℃23°C | 53 | kJ/m2 | ISO 179/1eU |
悬臂梁缺口冲击强度Notched Izod Impact Strength | ISO 180/1A | ||
-30℃-30°C | 10 | kJ/m2 | ISO 180-1A |
23℃23°C | 10 | kJ/m2 | ISO 180-1A |
悬臂梁无缺口冲击强度悬臂梁无缺口冲击强度 | |||
23℃23℃ | 34 | kJ/m2 | ISO 180/1U |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
热变形温度热变形温度 | |||
8.0 MPa,未退火8.0 MPa,未退火 | 215 | ℃ | ISO 75-2/C |
1.8 MPa,未退火1.8 MPa,未退火 | 270 | ℃ | ISO 75-2/A |
1.8 MPa,未退火1.8 MPa,未退火 | 265 | ℃ | ASTM D648 |
0.45 MPa,退火0.45 MPa,退火 | 280 | ℃ | ASTM D648 |
玻璃化转变温度Glass Transition Temperature 33 | 90.0 | ℃ | ISO 11357-2 |
熔融温度Melting Temperature 55 | 280 | ℃ | ISO 11357-3 |
线性热膨胀系数线性热膨胀系数 | |||
TDTD | 4.2E-5 | 1/℃ | ISO 11359-2 |
MDMD | 2.6E-5 | 1/℃ | ISO 11359-2 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
表面电阻率Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
体积电阻率Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
介电强度Electric Strength 44 | 15 | kV/mm | ASTM D149 |
介电强度Electric Strength | 28 | kV/mm | IEC 60243-1 |
介电常数Dielectric Constant | ASTM D150 | ||
1 kHz1 kHz | 3.50 | ASTM D150 | |
1 MHz1 MHz | 3.50 | ASTM D150 | |
相对电容率相对电容率 | |||
1 MHz1 MHz | 4.10 | IEC 60250 | |
耗散因数Dissipation Factor | ASTM D150 | ||
1 MHz1 MHz | 2.0E-3 | IEC 60250 | |
1 kHz1 kHz | 1.0E-3 | ASTM D150 | |
1 MHz1 MHz | 1.0E-3 | ASTM D150 | |
耐电弧性Arc Resistance | 134 | sec | ASTM D495 |
相比漏电起痕指数Comparative Tracking Index | 125 | V | IEC 60112 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
阻燃等级Flame Rating | UL 94 | ||
0.38 mm0.38 mm | V-0 | UL 94 | |
1.50 mm1.5 mm | V-0 | UL 94 | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
CSA Rating(8.40E-7 mm)CSA Rating (8.40E-7 mm) | A00 | CSA F-1 | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
拉伸模量Tensile Modulus | 14700 | MPa | ISO 527-2/1A/1 |
拉伸强度拉伸强度 | |||
断裂,23℃断裂,23℃ | 200 | MPa | ASTM D638 |
断裂断裂 | 195 | MPa | ISO 527-2/1A/5 |
拉伸应变拉伸应变 | |||
断裂,23℃断裂,23℃ | 2.0 | % | ASTM D638 |
断裂断裂 | 1.9 | % | ISO 527-2/1A/5 |
弯曲模量弯曲模量 | |||
23℃23℃ | 14500 | MPa | ISO 178 |
弯曲强度Flexural Stress 22 | 285 | MPa | ISO 178 |
洛氏硬度洛氏硬度 | |||
M 级M 级 | 100 | ASTM D785 | |
M 级M 级 | 100 | ISO 2039-2 | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
密度Specific Gravity | 1.60 | g/cm3 | ASTM D792 |
特定体积Specific Volume | 0.625 | cm3/g | ASTM D792 |
密度Density | 1.65 | g/cm3 | ISO 1183 |
熔体质量流动速率Melt Mass-Flow Rate (MFR) | 19 | g/10min | ASTM D1238 |
收缩率Molding Shrinkage | ISO 294-4 | ||
TDTD | 0.50 to 0.70 | % | ASTM D955 |
MDMD | 0.20 to 0.30 | % | ASTM D955 |
TDAcross Flow | 0.40 to 0.60 | % | ISO 294-4 |
MDFlow | 0.20 to 0.60 | % | ISO 294-4 |
吸水率吸水率 | |||
饱和,23℃饱和,23℃ | 0.020 | % | ISO 62 |
螺旋流动长度Spiral Flow | 21.5 | Internal Method | |
Specific Heat Capacity of MeltSpecific Heat Capacity of Melt | 1500 | J/kg/℃ | Internal Method |