江苏普及塑料有限公司
| 牌号简介About |
|---|
| Toyolac? 700-314是一种丙烯腈丁二烯苯乙烯(ABS)产品,。 特性包括: 阻燃/额定火焰 耐冲击 Toyolac? 700-314 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Applications of Toyolac? 700-314 include appliances, automotive, electrical/electronic applications and housings. Characteristics include: Flame Rated Impact Resistant |
产品描述Product Description
厂家：日本东丽Toray Plastics (Malaysia) Sdn. Bhd.
类别：ABSABS
性能特点：防火阻燃等级HB;HB
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.05 | g/cm3 | ASTM D792 |
| 密度Density (73°F) | 1.05 | g/cm3 | ISO 1183 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 220℃，10.0kg220℃/10.0 kg | 23 | g/10min | ISO 1133 |
| 收缩率Molding Shrinkage | 0.40 to 0.60 | % | 内部方法 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度简支梁缺口冲击强度 | |||
| 23℃23℃ | 17 | kJ/m2 | ISO 179 |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | ASTM D256 | ||
| -30℃，3.2mm-30°C, 3.20 mm | 120 | J/m | ASTM D256 |
| -30℃，12.7mm-30°C, 12.7 mm | 78 | J/m | ASTM D256 |
| 0℃，3.2mm0°C, 3.20 mm | 160 | J/m | ASTM D256 |
| 0℃，12.7mm0°C, 12.7 mm | 110 | J/m | ASTM D256 |
| 23℃，3.2mm23°C, 3.20 mm | 200 | J/m | ASTM D256 |
| 23℃，12.7mm23°C, 12.7 mm | 190 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火，6.4 mm1.8 MPa，未退火，6.40 mm | 87.0 | ℃ | ASTM D648 |
| 1.8 MPa，未退火1.8 MPa，未退火 | 82.0 | ℃ | ISO 75-2/A |
| 维卡软化温度Vicat Softening Temperature | 95.0 | ℃ | |
| 线性热膨胀系数线性热膨胀系数 | |||
| MDMD | 7.1E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度Tensile Strength | 50.0 | MPa | ASTM D638 |
| 屈服，23℃屈服，23℃ | 54.0 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 断裂，23℃断裂，23℃ | 18 | % | ISO 527-2 |
| 断裂断裂 | 35 | % | ASTM D638 |
| 弯曲模量Flexural Modulus | 2450 | MPa | ASTM D790 |
| 23℃23℃ | 2540 | MPa | ISO 178 |
| 弯曲强度Flexural Strength | 76.0 | MPa | ASTM D790 |
| 23℃23℃ | 81.0 | MPa | ISO 178 |
| 洛氏硬度洛氏硬度 | |||
| R 级R 计秤，23℃ | 115 | ISO 2039-2 | |
| R 级R 计秤，23℃ | 115 | ASTM D785 | |