江苏普及塑料有限公司
| 牌号简介About |
|---|
| 说明透明、高冲击、柔软的人造指甲 Description Transparency, High Impact, Softness Application Artificial nail |
产品描述Product Description
厂家：韩国LG化学LG Polymers India Pvt. Ltd.
类别：透明ABSABS transparent
加工条件：注射成型Injection Molding
性能特点：柔软性好; 透光性好; 冲击性能好;Good Clarity,High impact resistance,Soft
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度密度 / 比重 | 1.06 | g/cm3 | ASTM D792 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 220℃，10.0kg220℃/10.0 kg | 10 | g/10min | ASTM D1238 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃，3.2mm23°C, 3.20 mm | 240 | J/m | |
| 23℃，6.4mm23°C, 6.40 mm | 240 | J/m | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火，6.4 mm1.8 MPa，未退火，6.40 mm | 74.0 | ℃ | ASTM D648 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 透光率Transmittance | 89.0 | % | ASTM D1003 |
| 雾度Haze | 3.0 | % | ASTM D1003 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度洛氏硬度 | |||
| R 级R 级 | 88 | ASTM D785 | |
| 拉伸强度拉伸强度2 | |||
| 屈服，3.20 mm屈服，3.20 mm2 | 32.4 | MPa | ASTM D638 |
| 拉伸应变拉伸应变2 | |||
| 断裂，3.20 mm断裂，3.20 mm2 | 40 | % | ASTM D638 |
| 弯曲模量弯曲模量3 | |||
| 3.20 mm3.20 mm3 | 1470 | MPa | ASTM D790 |
| 弯曲强度弯曲强度3 | |||
| 3.20 mm3.20 mm3 | 49.0 | MPa | ASTM D790 |