Ryton? R-4
聚苯硫醚
40% 玻璃纤维增强材料
产品说明：
Ryton? R-4 and R-4-02 40% glass fiber reinforced polyphenylene sulfide compounds provide a good combination of mechanical and electrical properties with outstanding chemical resistance, even at elevated temperatures.
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.69 |
g/cm3 |
ASTM D792 |
| 收缩率 |
|
|
|
| 流动 : 3.20 mm |
0.20 |
% |
|
| 横向流动 : 3.20 mm |
0.50 |
% |
|
| 吸水率(23°C, 24 hr) |
0.020 |
% |
ASTM D570 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 洛氏硬度 |
|
|
ASTM D785 |
| M 级 |
104 |
|
ASTM D785 |
| R 级 |
122 |
|
ASTM D785 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度 |
|
|
|
| -- |
159 |
MPa |
ASTM D638 |
| -- |
150 |
MPa |
ISO 527-2 |
| 伸长率 |
|
|
|
| 断裂 |
1.1 |
% |
ASTM D638 |
| 断裂 |
1.2 |
% |
ISO 527-2 |
| 弯曲模量 |
|
|
|
| -- |
14500 |
MPa |
ASTM D790 |
| -- |
14000 |
MPa |
ISO 178 |
| 弯曲强度 |
|
|
|
| -- |
221 |
MPa |
ASTM D790 |
| -- |
220 |
MPa |
ISO 178 |
| 压缩强度 |
270 |
MPa |
ASTM D695 |
| 泊松比 |
0.38 |
|
|
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 |
|
|
|
| 3.18 mm |
91 |
J/m |
ASTM D256 |
| -- |
9.0 |
kJ/m2 |
ISO 180/A |
| 无缺口悬臂梁冲击 |
|
|
|
| 3.18 mm |
400 |
J/m |
ASTM D4812 |
| -- |
25 |
kJ/m2 |
ISO 180 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度(1.8 MPa, 未退火) |
265 |
°C |
ASTM D648 |
| 线形热膨胀系数 |
|
|
ASTM E831 |
| 流动 : -50 到 50°C |
2.0E-5 |
cm/cm/°C |
ASTM E831 |
| 流动 : 100 到 200°C |
1.5E-5 |
cm/cm/°C |
ASTM E831 |
| 横向 : -50 到 50°C |
4.0E-5 |
cm/cm/°C |
ASTM E831 |
| 横向 : 100 到 200°C |
8.0E-5 |
cm/cm/°C |
ASTM E831 |
| 导热系数 |
0.32 |
W/m/K |
|
| UL温度额定值 |
200 到 220 |
°C |
UL 746B |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+16 |
ohms |
ASTM D257 |
| 体积电阻率 |
1.0E+16 |
ohms·cm |
ASTM D257 |
| 介电强度 |
20 |
kV/mm |
ASTM D149 |
| 介电常数 |
|
|
ASTM D150 |
| 25°C, 1 kHz |
3.90 |
|
ASTM D150 |
| 25°C, 1 MHz |
3.80 |
|
ASTM D150 |
| 耗散因数 |
|
|
ASTM D150 |
| 25°C, 1 kHz |
2.0E-3 |
|
ASTM D150 |
| 25°C, 1 MHz |
2.0E-3 |
|
ASTM D150 |
| 耐电弧性 |
125 |
sec |
ASTM D495 |
| 相比耐漏电起痕指数(CTI) |
130 |
V |
UL 746 |
| Insulation Resistance1(90°C) |
1.0E+11 |
ohms |
|
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级(1.60 mm) |
V-0 5VA |
|
UL 94 |
| 极限氧指数 |
47 |
% |
ASTM D2863 |