General
Material Status	Commercial: Active
Availability	Latin AmericaNorth America
Additive	Mold Release
Features	BiocompatibleFood Contact AcceptableHigh Flow
Uses	AppliancesConstruction ApplicationsFluid HandlingMedical/Healthcare ApplicationsNon-specific Food ApplicationsPharmaceuticals
Agency Ratings
Appearance	Colors Available
Processing Method	Compounding ExtrusionInjection Molding

Physical	Nominal Value	Unit	Test Method
Density / Specific Gravity
--			ASTM D792
--		g/cm3	ISO 1183
Melt Mass-Flow Rate (MFR)(250°C/2.16 kg)		g/10 min	ASTM D1238
Melt Volume-Flow Rate (MVR)(250°C/2.16 kg)		cm3/10min	ISO 1133
Molding Shrinkage - Flow(0,126 in)		%	Internal Method
Water Absorption			ISO 62
Saturation, 73°F		%
Equilibrium, 73°F, 50% RH		%
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--2		psi	ASTM D638
--		psi	ISO 527-2/1
Tensile Strength
Yield3		psi	ASTM D638
Yield		psi	ISO 527-2/50
Break3		psi	ASTM D638
Break		psi	ISO 527-2/50

PBT VALOX HX215HP

特性

PBT是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。这些材料在很广的环境条件下都有很好的稳定性。PBT吸湿特性很弱。非增强型PBT的张力强度为50MPa，玻璃添加剂型的PBT张力强度为170MPa。玻璃添加剂过多将导致材料变脆。PBT的结晶很迅速，这将导致因冷却不均匀而造成弯曲变形。对于有玻璃添加剂类型的材料，流程方向的收缩率可以减小，但与流程垂直方向的收缩率基本上和普通材料没有区别。一般材料收缩率在1.5%~2.8%之间。含30%玻璃添加剂的材料收缩0.3%~1.6%之间。熔点（225℃）和高温变形温度都比PET材料要低。维卡软化温度大约为170℃。玻璃化转换温度（glass trasitio temperature）在22℃到43℃之间。由于PBT的结晶速度很高，因此它的粘性很低，塑件加工的周期时间一般也较低。

三、PBT塑料的粘接：

根据不同需要，可以选择以下粘合剂：

1. TG-3200：单组分常温固化软弹性防震粘合剂，耐高低温，但粘接速度慢，胶水通常要1天或几天时间才能固化完毕。

2. TS-8602瞬间粘接剂，可以数秒钟或数十秒钟快速粘合PBT，但胶层硬脆，不耐水。

3. TE-9270类，双组分胶，胶层柔软，适合PBT大面积粘接或复合。但耐高温性能较差。

4.TE-9249类胶：双组分胶，耐高温。

应用范围

家用器具（食品加工刀片、真空吸尘器元件、电风扇、头发干燥机壳体、咖啡器皿等），电器元件（开关、电机壳、保险丝盒、计算机键盘按键等），汽车工业（散热器格窗、车身嵌板、车轮盖、门窗部件等）。