江苏普及塑料有限公司
| 牌号简介About |
|---|
| fcfc-abs树脂ag15a0符合UL、SGS和环保证书的要求。 |
产品描述Product Description
厂家：台湾台化台化宁波
类别：ABSABS
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级HB;HB
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.05 | g/cm3 | ASTM D792 |
| 密度Density (73°F) | 1.05 | g/cm3 | ISO 1183 |
| 熔体质量流动速率Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200℃，5.0kg200°C/5.0 kg | 1.7 | g/10min | ASTM D1238 |
| 220℃，10.0kg220°C/10.0 kg | 19 | g/10min | ASTM D1238 |
| 熔体质量流动速率Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 200℃，5.0kg200°C/5.0 kg | 1.7 | g/10min | ISO 1133 |
| 220℃，10.0kg220°C/10.0 kg | 19 | g/10min | ISO 1133 |
| 收缩率收缩率 | |||
| MDMD | 0.40 to 0.70 | % | 内部方法 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃，6.4mm23°C, 6.35 mm | 200 | J/m | ISO 180 |
| 23℃，6.4mm23°C, 6.35 mm | 200 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，退火1.8 MPa，退火2 | 95.0 | ℃ | ISO 75-2/A |
| 1.8 MPa，退火1.8 MPa，退火2 | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa，未退火，12.7 mm1.8 MPa，未退火，12.7 mm | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa，未退火，12.7 mm1.8 MPa，未退火，12.7 mm | 85.0 | ℃ | ISO 75-2/A |
| 维卡软化温度Vicat Softening Temperature | 104 | ℃ | ASTM D1525 3 |
| 维卡软化温度Vicat Softening Temperature | 104 | ℃ | ISO 306/A |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 1.50 mm，所有颜色1.5 mm，All Colors | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度 | |||
| 屈服，23℃屈服，23℃ | 52.0 | MPa | ISO 527-2 |
| 23℃23℃ | 52.0 | MPa | ASTM D638 |
| 弯曲模量弯曲模量 | |||
| 23℃23℃ | 2650 | MPa | ASTM D790 |
| 23℃23℃ | 2650 | MPa | ISO 178 |
| 弯曲强度弯曲强度 | |||
| 23℃23℃ | 83.4 | MPa | ASTM D790 |
| 23℃23℃ | 84.0 | MPa | ISO 178 |
| 洛氏硬度洛氏硬度 | |||
| R 级R 计秤，23℃ | 110 | ASTM D785 | |
| R 级R 计秤，23℃ | 110 | ISO 2039-2 | |