Elastollan? 1190A10
热塑性聚氨酯弹性体（聚醚）
产品说明：
Elastollan? 1190A is specifically formulated for extruded profile, tubing, sheet and film applications. It exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan? 1190A conforms to the FDA food contact section, book 21, section 177.2600. Elastollan? 1190A also has NSF Standard 61 "Water Contact Material" certification.. Elastollan? 1190A is supplied uncolored in diced or pelletized form.
| 基本信息 |
|
| 特性 |
- 低温下的柔性
- 抗菌性
- 良好的撕裂强度
- 良好耐磨损性
- 韧性良好
- 食品接触的合规性
- 水解稳定
|
| 机构评级 |
- FDA 21 CFR 177.2600
- NSF 61
|
| 外观 |
|
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.13 |
g/cm3 |
ASTM D792 |
| 熔流率（熔体流动速率） |
|
|
ASTM D1238 |
| 190°C/10.0 kg |
10 到 20 |
g/10 min |
ASTM D1238 |
| 190°C/21.6 kg |
10 到 40 |
g/10 min |
ASTM D1238 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 肖氏硬度(邵氏 A) |
90 |
|
ASTM D2240 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量(注塑) |
31.0 |
MPa |
ASTM D412 |
| 弯曲模量(注塑) |
29.0 |
MPa |
ASTM D790 |
| 泰伯耐磨性 |
45.0 |
mg |
ASTM D1044 |
| Abrasion - DIN |
25 |
mm3 |
DIN 53516 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| Softening Point - DMA |
100 |
°C |
内部方法 |
| 弹性体 |
额定值 |
单位制 |
测试方法 |
| 拉伸应力 |
|
|
ASTM D412 |
| 100%应变 |
12.4 |
MPa |
ASTM D412 |
| 300%应变 |
27.6 |
MPa |
ASTM D412 |
| 抗张强度 |
37.2 |
MPa |
ASTM D412 |
| 伸长率(断裂) |
460 |
% |
ASTM D412 |
| 撕裂强度1 |
128 |
kN/m |
ASTM D624 |
| 压缩永久变形 |
|
|
ASTM D395B |
| 23°C, 22 hr |
25 |
% |
ASTM D395B |
| 70°C, 22 hr |
45 |
% |
ASTM D395B |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 玻璃转化温度 |
-35.0 |
°C |
内部方法 |
| 维卡软化温度 |
120 |
°C |
ASTM D1525 |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
100 到 110 |
°C |
|
| 干燥时间 |
2.0 到 3.0 |
hr |
|
| 建议的最大水分含量 |
0.030 |
% |
|
| 料筒后部温度 |
190 到 220 |
°C |
|
| 料筒中部温度 |
190 到 220 |
°C |
|
| 料筒前部温度 |
190 到 220 |
°C |
|
| 射嘴温度 |
210 到 225 |
°C |
|
| 挤出 |
额定值 |
单位制 |
|
| 干燥温度 |
100 到 110 |
°C |
|
| 干燥时间 |
2.0 到 3.0 |
hr |
|
| 料筒1区温度 |
170 到 210 |
°C |
|
| 料筒3区温度 |
170 到 210 |
°C |
|
| 料筒5区温度 |
170 到 210 |
°C |
|
| 接头温度 |
200 到 220 |
°C |
|
| 口模温度 |
195 到 215 |
°C |
|