江苏普及塑料有限公司
| 牌号简介About |
|---|
| POLYLAC? PA-717C是一种丙烯腈丁二烯苯乙烯(ABS)产品,。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 典型应用领域为:汽车行业。 特性包括: 阻燃/额定火焰 通过 ROHS 认证 耐冲击 POLYLAC? PA-717C is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include: Flame Rated RoHS Compliant Impact Resistant |
产品描述Product Description
厂家：台湾奇美CHI MEI CORPORATION
类别：ABSABS
性能特点：防火阻燃等级HB;HB
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | |||
| ---- 33 | 1.04 | g/cm3 | ASTM D792 |
| 23℃23°C | 1.04 | g/cm3 | ISO 1183 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 200℃，5.0kg200℃/5.0 kg | 1.3 | g/10min | ASTM D1238 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 220℃，10 kg220℃/10.0 kg | 16.0 | cm3/10min | ISO 1133 |
| 收缩率Molding Shrinkage | 0.40 到 0.70 | % | ISO 294-4 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179 | ||
| -30℃-30°C | 13 | kJ/m2 | ISO 179 |
| 23℃23°C | 27 | kJ/m2 | ISO 179 |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃，3.2mm23°C, 3.20 mm | 290 | J/m | ASTM D256 |
| 23℃，6.4mm23°C, 6.40 mm | 250 | J/m | ASTM D256 |
| -30℃-30°C | 12 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 25 | kJ/m2 | ISO 180-1A |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | |||
| 1.8 MPa，未退火264 psi, Unannealed | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa，未退火264 psi, Unannealed | 82.0 | ℃ | ISO 75-2/A |
| 1.8 MPa，退火264 psi, Annealed | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa，退火264 psi, Annealed | 97.0 | ℃ | ISO 75-2/A |
| 维卡软化温度Vicat Softening Temperature | |||
| ---- | 104 | ℃ | ASTM D1525 7 |
| A50-- | 103 | ℃ | ISO 306/A50 |
| B50-- | 98.0 | ℃ | ISO 306 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MDMD | 8.8E-5 | 1/℃ | ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级1.5 mm | |||
| 1.50 mm | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度洛氏硬度 | |||
| R 级R 级 | 115 | ASTM D785 | |
| 拉伸强度Tensile Strength | |||
| 屈服屈服 44 | 42.1 | MPa | ASTM D638 |
| 屈服Yield | 44.0 | MPa | ISO 527-2/50 |
| 断裂Break | 33.0 | MPa | ISO 527-2/50 |
| 拉伸应变Tensile Elongation | |||
| 断裂Break 44 | 30 | % | ASTM D638 |
| 断裂Break | 30 | % | ISO 527-2/50 |
| 弯曲模量Flexural Modulus | |||
| ---- 55 | 2410 | MPa | ASTM D790 |
| ---- 66 | 1900 | MPa | ISO 178 |
| 弯曲强度Flexural Strength | |||
| ---- 55 | 70.3 | MPa | ASTM D790 |
| ---- 66 | 69.0 | MPa | ISO 178 |