| 牌号简介About |
|---|
| POLYLAC? PA-747S是一种丙烯腈丁二烯苯乙烯(ABS)产品,。 它可以通过挤出进行加工,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 特性包括: 阻燃/额定火焰 通过 ROHS 认证 POLYLAC? PA-747S is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion and is available in Africa Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include: Flame Rated RoHS Compliant |
产品描述Product Description
厂家：台湾奇美CHI MEI CORPORATION
类别：ABSABS
加工条件：挤出Extrusion
性能特点：防火阻燃等级HB;HB
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | |||
| ---- 33 | 1.03 | g/cm3 | ASTM D792 |
| 23℃23°C | 1.04 | g/cm3 | ISO 1183 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 200℃，5.0kg200℃/5.0 kg | 0.50 | g/10min | ASTM D1238 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 220℃，10 kg220℃/10.0 kg | 2.50 | cm3/10min | ISO 1133 |
| 收缩率Molding Shrinkage | 0.40 到 0.70 | % | ISO 294-4 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179 | ||
| -30℃-30°C | 28 | kJ/m2 | ISO 179 |
| 23℃23°C | 39 | kJ/m2 | ISO 179 |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃，3.2mm23°C, 3.20 mm | 400 | J/m | ASTM D256 |
| 23℃，6.4mm23°C, 6.40 mm | 350 | J/m | ASTM D256 |
| -30℃-30°C | 26 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 37 | kJ/m2 | ISO 180-1A |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | |||
| 1.8 MPa，未退火264 psi, Unannealed | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa，未退火264 psi, Unannealed | 83.0 | ℃ | ISO 75-2/A |
| 1.8 MPa，退火264 psi, Annealed | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa，退火264 psi, Annealed | 99.0 | ℃ | ISO 75-2/A |
| 维卡软化温度Vicat Softening Temperature | |||
| ---- | 103 | ℃ | ASTM D1525 7 |
| A50-- | 106 | ℃ | ISO 306/A50 |
| B50-- | 101 | ℃ | ISO 306 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MDMD | 9.1E-5 | 1/℃ | ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级1.5 mm | |||
| 1.50 mm | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度洛氏硬度 | |||
| R 级R 级 | 102 | ASTM D785 | |
| 拉伸强度Tensile Strength | |||
| 屈服屈服 44 | 38.1 | MPa | ASTM D638 |
| 屈服Yield | 41.0 | MPa | ISO 527-2/50 |
| 断裂Break | 30.0 | MPa | ISO 527-2/50 |
| 拉伸应变Tensile Elongation | |||
| 断裂Break 44 | 40 | % | ASTM D638 |
| 断裂Break | 25 | % | ISO 527-2/50 |
| 弯曲模量Flexural Modulus | |||
| ---- 55 | 2070 | MPa | ASTM D790 |
| ---- 66 | 1700 | MPa | ISO 178 |
| 弯曲强度Flexural Strength | |||
| ---- 55 | 60.7 | MPa | ASTM D790 |
| ---- 66 | 61.0 | MPa | ISO 178 |