LNP? LUBRICOMP? RN001S compound
聚酰胺66
产品说明：
LNP LUBRICOMP RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized.
Also known as: LNP* LUBRICOMP* Compound R- HS
Product reorder name: RN001S
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
|
|
|
| -- |
1.16 |
g/cm3 |
ASTM D792 |
| -- |
1.17 |
g/cm3 |
ISO 1183 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
| --1 |
4140 |
MPa |
ASTM D638 |
| -- |
3910 |
MPa |
ISO 527-2/1 |
| 抗张强度 |
|
|
|
| 屈服 |
84.1 |
MPa |
ASTM D638 |
| 屈服 |
69.0 |
MPa |
ISO 527-2 |
| 断裂 |
84.1 |
MPa |
ASTM D638 |
| 断裂 |
69.0 |
MPa |
ISO 527-2 |
| 伸长率 |
|
|
|
| 屈服 |
2.9 |
% |
ASTM D638 |
| 屈服 |
2.1 |
% |
ISO 527-2 |
| 断裂 |
3.8 |
% |
ASTM D638 |
| 断裂 |
42 |
% |
ISO 527-2 |
| 弯曲模量 |
|
|
|
| -- |
3450 |
MPa |
ASTM D790 |
| -- |
3400 |
MPa |
ISO 178 |
| 弯曲应力 |
107 |
MPa |
ISO 178 |
| 摩擦系数 |
|
|
ASTM D3702 Modified |
| 与自身 - 动态 |
0.75 |
|
ASTM D3702 Modified |
| 与自身 - 静态 |
0.55 |
|
ASTM D3702 Modified |
| 磨损因数 - Washer |
103 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 |
|
|
|
| 23°C |
27 |
J/m |
ASTM D256 |
| 23°C2 |
2.8 |
kJ/m2 |
ISO 180/1A |
| 无缺口悬臂梁冲击 |
|
|
|
| 23°C |
1100 |
J/m |
ASTM D4812 |
| 23°C3 |
54 |
kJ/m2 |
ISO 180/1U |
| 装有测量仪表的落镖冲击(23°C, Energy at Peak Load) |
2.30 |
J |
ASTM D3763 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
| 0.45 MPa, 未退火, 3.20 mm |
231 |
°C |
ASTM D648 |
| 0.45 MPa, 未退火, 64.0 mm 跨距4 |
223 |
°C |
ISO 75-2/Bf |
| 1.8 MPa, 未退火, 3.20 mm |
76.7 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距5 |
301 |
°C |
ISO 75-2/Af |
| 注射 |
额定值 |
单位制 |
|
| 干燥温度 |
82.2 |
°C |
|
| 干燥时间 |
4.0 |
hr |
|
| 建议的最大水分含量 |
0.15 到 0.25 |
% |
|
| 料筒后部温度 |
266 到 277 |
°C |
|
| 料筒中部温度 |
282 到 293 |
°C |
|
| 料筒前部温度 |
293 到 304 |
°C |
|
| 加工（熔体）温度 |
277 到 288 |
°C |
|
| 模具温度 |
82.2 到 93.3 |
°C |
|
| 背压 |
0.172 到 0.344 |
MPa |
|
| 螺杆转速 |
30 到 60 |
rpm |
|
| 备注 |
| 1 . |
50 mm/min |
| 2 . |
80*10*4 |
| 3 . |
80*10*4 |
| 4 . |
80*10*4 mm |
| 5 . |
80*10*4 mm |