ENGAGE? HM 7387聚烯烃弹性体是一种乙烯-丁烯共聚物,比其他市售聚烯烃弹性体具有更高的分子量、更好的韧性和更高的熔融强度。它可以作为SEBS的延长剂,在硬TPO中提供较低的光泽,为柔性软接触化合物提供基础,非常适合电线和电缆等挤压应用。ENGAGE? HM 7387还可用于各种热塑性树脂的冲击改性。主要特点:颗粒状高熔融强度提高韧性滑石粉(未经处理,1微米)应用:SEBS软触化合物聚合物改性延长剂降低光泽TPOS电线和电缆冲击改性 ENGAGE? HM 7387 Polyolefin Elastomer is an ethylene-butene copolymer that has higher molecular weight, better toughness, and higher melt strength than other commercially available polyolefin elastomers. It can serve as an extender for SEBS, impart lower gloss in hard TPOs, provide the basis for flexible soft-touch compounds, and is well suited for extruded applications such as wire and cable. ENGAGE HM 7387 is also useful for impact modification of various thermoplastic resins. Main Characteristics: Pellet form High melt strength Improved toughness Talc dusted (untreated, 1 μm) Applications: Polymer modification Extender for SEBS Soft-touch compounds Reduced gloss TPOs Wire and cable Impact modification |
产品描述Product Description
厂家:美国陶氏DOW
类别:TPO(POE)Polyolefin Elastomer
技术参数Technical Data | |||
---|---|---|---|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
密度Specific Gravity | 0.870 | g/cm3 | ASTM D792 |
熔体质量流动速率熔体质量流动速率 | |||
190℃,2.16kg190℃/2.16 kg | 0.50 | g/10min | ASTM D1238 |
门尼粘度门尼粘度 | |||
ML 1+4,121℃ML 1+4,121℃ | 54 | MU | ASTM D1646 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
撕裂强度Tear Strength 33 | 40.6 | kN/m | ASTM D624 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
玻璃化转变温度Glass Transition Temperature | -52.0 | ℃ | 内部方法 |
维卡软化温度Vicat Softening Temperature | 46.0 | ℃ | ASTM D1525 |
熔融温度溶融温度4 | |||
DSCDSC4 | 50.0 | ℃ | 内部方法 |
结晶峰温度结晶峰温度 | |||
DSCDSC | 38.0 | ℃ | 内部方法 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
邵氏硬度Durometer Hardness | ASTM D2240 | ||
邵氏 A,模压成型Shore A, Compression Molded | 66 | ASTM D2240 | |
邵氏 D,模压成型Shore D, Compression Molded | 22 | ASTM D2240 | |
拉伸模量拉伸模量2 | |||
100% 正割,模压成型100% 正割,模压成型2 | 2.90 | MPa | ASTM D638 |
拉伸强度拉伸强度2 | |||
断裂,模压成型断裂,模压成型2 | 9.10 | MPa | ASTM D638 |
拉伸应变拉伸应变2 | |||
断裂,模压成型断裂,模压成型2 | 810 | % | ASTM D638 |
弯曲模量Flexural Modulus | ASTM D790 | ||
1% 正割,模压成型1% Secant : Compression Molded | 12.2 | MPa | ASTM D790 |
2% 正割,模压成型2% Secant : Compression Molded | 11.5 | MPa | ASTM D790 |