PC LEXAN LUX7169
LEXAN LUX7169 is an injection moldable polycarbonate (PC) with an MVR (300°C/1.2kg) 22. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0@0.9mm rating. It is designed for high light reflectance and shielding applications with good UV weathering capability.
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.38g/cc | 1.38g/cc | ASTM D792 |
Density | 1.38g/cc | 0.0499lb/in3 | ISO 1183 |
Water Absorption | 0.350 % | 0.350 % | 23°C/sat; ISO 62 |
Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
Linear Mold Shrinkage, Flow | 0.00500-0.00700cm/cm @Thickness 3.20 mm |
0.00500-0.00700in/in @Thickness 0.126 in |
SABIC method |
Melt Flow | 22.0g/10 min @Load 1.20 kg, Temperature 300 °C |
22.0g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
22.0g/10 min @Load 1.20 kg, Temperature 300 °C |
22.0g/10 min @Load 2.65 lb, Temperature 572 °F |
cm3/10 min; ISO 1133 | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 45.0MPa | 6530psi | 50 mm/min; ASTM D638 |
Tensile Strength, Yield | 60.0MPa | 8700psi | 50 mm/min; ASTM D638 |
Elongation at Break | 11.0 % | 11.0 % | 50 mm/min; ASTM D638 |
PC LEXAN LUX7169
特性:
为非结晶性热塑性塑料,优质的耐热性能、良好的透明度和极高的耐冲击强度等物理机械性能。
优点:
1.具高强度及弹性系数、高冲击强度、使用温度范围广;
2.高度透明性及自由染色性;
3.H.D.T.高;
4.耐疲劳性差;
5、耐候性佳;
6.电气特性优;
7.无味无臭对人体无害符合卫生安全;
8.成形收缩率低、尺寸安定性良好。
应用
PC工程塑料的三大应用领域是玻璃装配业、汽车工业和电子、电器工业,其次还有工业机械零件、光盘、包装、计算机等办公室设备、医疗及保健、薄膜、休闲和防护器材等。PC可用作门窗玻璃,PC层压板广泛用于银行、使馆、拘留所和公共场所的防护窗,用于飞机舱罩,照明设备、工业安全档板和防弹玻璃。
汽车制造业
聚碳酸酯具有良好的抗冲击、抗热畸变性能,而且耐候性好、硬度高,因此适用于生产轿车和轻型卡车的各种零部件,其主要集中在照明系统、仪表板、加热板、除霜器及聚碳酸酯合金制的保险杠等。
建材行业
聚碳酸酯板材具有良好的透光性,抗冲击性,耐紫外线辐射及其制品的尺寸稳定性和良好的成型加工性能,使其比建筑业传统使用的无机玻璃具有明显的技术性能优势。中国建有聚碳酸酯建材中空板生产线20余条,年需用聚碳酸酯7万吨左右,到2005年达到14万吨。