东莞市铭汇塑胶有限公司
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.41 g/cc | 0.0509 lb/in3 | DAM; ISO 1183 |
| Water Absorption | 1.7 %
@Temperature 23.0 °C
|
1.7 %
@Temperature 73.4 °F
|
Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 5.4 %
@Temperature 23.0 °C
|
5.4 %
@Temperature 73.4 °F
|
Saturation, immersed; DAM; ISO 62, Similar to | |
| 线性成型收缩率,Flow | 0.0020 cm/cm
@Thickness 2.00 mm
|
0.0020 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.0060 cm/cm
@Thickness 2.00 mm
|
0.0060 in/in
@Thickness 0.0787 in
|
DAM; ISO 294-4 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 128 MPa
@Temperature 23.0 °C
|
18600 psi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 185 MPa
@Temperature 23.0 °C
|
26800 psi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 伸长率 (断裂) | 3.5 %
@Temperature 23.0 °C
|
3.5 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 7.3 %
@Temperature 23.0 °C
|
7.3 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| Elongation at Yield | 5.0 %
@Temperature 23.0 °C
|
5.0 %
@Temperature 73.4 °F
|
DAM; ISO 527 |
| 22 %
@Temperature 23.0 °C
|
22 %
@Temperature 73.4 °F
|
50%RH; ISO 527 | |
| 拉伸模量 | 7.50 GPa
@Temperature 23.0 °C
|
1090 ksi
@Temperature 73.4 °F
|
50%RH; ISO 527 |
| 12.2 GPa
@Temperature 23.0 °C
|
1770 ksi
@Temperature 73.4 °F
|
DAM; ISO 527 | |
| 悬壁梁缺口冲击强度 | 18.0 kJ/m2
@Temperature -30.0 °C
|
8.57 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 180/1A |
| 19.0 kJ/m2
@Temperature -30.0 °C
|
9.04 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 180/1A | |
| 24.0 kJ/m2
@Temperature 23.0 °C
|
11.4 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 180/1A | |
| 30.0 kJ/m2
@Temperature 23.0 °C
|
14.3 ft-lb/in2
@Temperature 73.4 °F
|
50%RH; ISO 180/1A | |
| 简支梁无缺口冲击强度 | 10.5 J/cm2
@Temperature -30.0 °C
|
50.0 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eU |
| 11.0 J/cm2
@Temperature 23.0 °C
|
52.3 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eU | |
| 11.3 J/cm2
@Temperature 23.0 °C
|
53.8 ft-lb/in2
@Temperature 73.4 °F
|
50%RH; ISO 179/1eU | |
| 11.8 J/cm2
@Temperature -30.0 °C
|
56.1 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 1.70 J/cm2
@Temperature -30.0 °C
|
8.09 ft-lb/in2
@Temperature -22.0 °F
|
DAM; ISO 179/1eA |
| 1.80 J/cm2
@Temperature -30.0 °C
|
8.57 ft-lb/in2
@Temperature -22.0 °F
|
50%RH; ISO 179/1eA | |
| 2.40 J/cm2
@Temperature 23.0 °C
|
11.4 ft-lb/in2
@Temperature 73.4 °F
|
DAM; ISO 179/1eA | |
| 3.30 J/cm2
@Temperature 23.0 °C
|
15.7 ft-lb/in2
@Temperature 73.4 °F
|
50%RH; ISO 179/1eA |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 熔融温度 | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 载荷下热变形温度(1.8 MPa) | 212 °C | 414 °F | DAM; ISO 75-1/-2 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 270 °C | 518 °F | DAM; Optimum |
| 260 - 280 °C | 500 - 536 °F | DAM | |
| 模具温度 | 50.0 - 100 °C | 122 - 212 °F | DAM |
| 80.0 °C | 176 °F | DAM; optimum | |
| 干燥温度 | 80.0 °C | 176 °F | DAM |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| 水分含量 | = 0.20 % | = 0.20 % | DAM |
| 材料描述 | 测试方法 | |
|---|---|---|
| 形式 | Pellets | DAM |
| Generic | PA66 | DAM |
| Material Status | Preliminary Data | DAM |
| 加工方法 | Injection Molding | DAM |
| 产品分类 | Toughened Resins | DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |