PC LEXAN LUX2614

Lexan LUX2614G (EXRL0944) is a diffusive, high viscosity, uv stabilized, flame retardant polycarbonate with improved light transmission and providing good colorstability under heat exposure. Developed for injection molding LED applications

Information provided by SABIC

Physical Properties	Metric	English	Comments
Specific Gravity	1.20g/cc	1.20g/cc	ASTM D792
	1.20g/cc	1.20g/cc	ASTM D792
Density	1.19g/cc	0.0430lb/in3	ASTM D792
Water Absorption	0.150 %	0.150 %	24 hours; ASTM D570
Moisture Absorption at Equilibrium	0.350 %	0.350 %	ASTM D570
	0.580 % @Temperature 100 °C	0.580 % @Temperature 212 °F	ASTM D570
Linear Mold Shrinkage, Flow	0.00500-0.00700cm/cm @Thickness 3.20 mm	0.00500-0.00700in/in @Thickness 0.126 in	SABIC method
Melt Flow	7.00g/10 min @Load 1.20 kg, Temperature 300 °C	7.00g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
	7.00g/10 min @Load 1.20 kg, Temperature 300 °C	7.00g/10 min @Load 2.65 lb, Temperature 572 °F	cm3/10 min; ISO 1133
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	70.0	70.0	ASTM D785
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength at Break	63.0MPa	9140psi	50 mm/min; ISO 527

PC LEXAN LUX2614

塑料的处理

PC塑胶原料的吸水率较大，加工前一定要预热干燥，纯PC干燥120℃，改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下，可100%的使用再生料，实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒，否则会严重损坏成品的性质。

注塑机选用

PC塑料制品由于成本及其它方面的原因，多用改性材料，特别是电工产品，还须增加防火性能，在阻燃的PC和其它塑料合金产品成型时，对注塑机塑化系统的要求是混合好、耐腐蚀，常规的塑化螺杆难以做到，在选购时，一定要预先说明。

主要优点

1．具高强度及弹性系数、高冲击强度、使用温度范围广；

2．高度透明性及自由染色性；

3．成形收缩率低、尺寸安定性良好；

4．耐疲劳性佳；

5．耐候性佳；

6．电气特性优。

性能特点:良好的流动性;脱模性能良好;

粘度，高；光学透明性好、抗冲击强度高；

并具有优异的热安稳性、耐蠕变性、抗寒性、电绝缘性和阻燃性等。

加工方法:薄膜挤出；吹塑成型；挤出成型；热成型；树脂传递成型；涂层；砑光；注射成型也是最重要的加工方法之一；

用途:在透明建筑板材、电子电器、光盘、汽车工业、机械、光学、医药等领域得到广泛运用。

PC塑料物理性能以及加工

低温-45度聚碳酸酯无色透明，耐热，抗冲击，阻燃BI级，在普通运用温度内都有出色的机械功用。