| 牌号简介About |
|---|
| Noryl PX1134是一种未填充材料，VICAT B/120为120？c根据ISO 306。Noryl PX1134提供了改进的冲击性能，以满足汽车行业的标准ECE仪表板冲击测试。提供多种颜色，满足各种汽车内饰颜色标准。 NORYL PX1134 is an unfilled material with a Vicat B/120 of 120?C according ISO 306. NORYL PX1134 offers improved impact performance to meet the standard ECE dashboard impact tests in the automotive industry. Available in several colours, which meet the various automotive standards for interior colours. |
产品描述Product Description
厂家：沙特沙伯基础SABIC
类别：PPO(PPE)+PSPPO(PPE)+PS
用途：电气/电子应用领域;汽车领域的应用;汽车内部零件;
加工条件：注射成型Injection Molding
性能特点：冲击性能好;High impact resistance
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.06 | g/cm3 | ISO 1183 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 280℃，5 kg280℃/5.0 kg | 10.0 | cm3/10min | ISO 1133 |
| 收缩率收缩率2 | |||
| MDMD2 | 0.50 到 0.70 | % | 内部方法 |
| 吸水率Water Absorption | |||
| 饱和，23℃Saturation, 73°F | 0.14 | % | |
| 平衡，23℃，50% RHEquilibrium, 73°F, 50% RH | 0.060 | % | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度简支梁缺口冲击强度55 | |||
| -30℃-30°C | 14 | kJ/m2 | |
| 23℃23°C | 19 | kJ/m2 | |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度66 | |||
| -30℃-30°C | 10 | kJ/m2 | |
| 23℃23°C | 18 | kJ/m2 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度77 | |||
| 0.45 MPa，未退火，100 mm跨距0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | 120 | ℃ | ISO 75-2/Be |
| 1.8 MPa，未退火，100 mm跨距1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | 105 | ℃ | ISO 75-2/Ae |
| 维卡软化温度Vicat Softening Temperature | |||
| A50-- | 130 | ℃ | ISO 306/A50 |
| B50-- | 115 | ℃ | ISO 306 |
| B120-- | 125 | ℃ | ISO 306/B120 |
| 球压测试球压测试 | |||
| 73~77℃73 到 77℃ | 通过 | IEC 60695-10-2 | |
| 线性热膨胀系数CLTE | |||
| MD：23~80℃Flow : 73 to 176°F | 7.0E-5 | 1/℃ | |
| TD：23~80℃Transverse : 73 to 176°F | 9.0E-5 | 1/℃ | |
| 导热系数Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度介电强度 | |||
| 3.2 mm，在油中3.20 mm，在油中 | 17 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | |||
| 50 Hz50 Hz | 2.70 | ||
| 60 Hz60 Hz | 2.70 | ||
| 1 MHz1 MHz | 2.60 | ||
| 耗散因数Dissipation Factor | |||
| 50 Hz50 Hz | 4.0E-4 | ||
| 60 Hz60 Hz | 4.0E-4 | ||
| 1 MHz1 MHz | 9.0E-4 | ||
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 1.60 mm1.6 mm，Testing by SABIC | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 球压硬度球压硬度 | |||
| H358/30H 358/30 | 80.0 | MPa | ISO 2039-1 |
| 拉伸模量Tensile Modulus | 2100 | MPa | ISO 527-1-2 |
| 拉伸强度Tensile Stress | |||
| 屈服Yield | 40.0 | MPa | |
| 断裂Break | 40.0 | MPa | |
| 拉伸应变Tensile Strain | |||
| 屈服Yield | 3.0 | % | |
| 断裂Break | 40 | % | |
| 弯曲模量弯曲模量33 | 1900 | MPa | ISO 178 |
| 弯曲强度弯曲应力3,43 ,4 | 85.0 | MPa | ISO 178 |
| 泰伯耐磨性泰伯耐磨性 | |||
| 1000 周期，1000 g，CS-17 转轮1000 周期，1000 g，CS-17 转轮 | 65.0 | mg | 内部方法 |