江苏普及塑料有限公司
| 牌号简介About |
|---|
| PPE + PS共混物。未填充的无卤阻燃性能。UL94 V0/5VA。UL746C F1。介电强度。适用于E/E市场室内/室外应用。 PPE+PS blend. Unfilled. Halogen-Free FR performance. UL94 V0/5VA. UL746C F1. Dielectric Strength. Suitable for E/E market indoor/outdoor applications. |
产品描述Product Description
厂家：沙特沙伯基础SABIC
类别：PPO(PPE)+PSPPO(PPE)+PS
用途：电气/电子应用领域;电子显示器;建筑应用领域;电器用具;汽车的发动机罩下的零件;
加工条件：注射成型Injection Molding
性能特点：无卤; 阻燃;Halogen free,Flame Characteristics
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度密度 / 比重 | 1.11 | g/cm3 | ASTM D792 |
| 收缩率Molding Shrinkage | |||
| MD：3.2 mm流动 : 3.20 mm | 0.50 到 0.70 | % | |
| TD：3.2 mm横向流动 : 3.20 mm | 0.50 到 0.70 | % | |
| 室外适用性Outdoor Suitability | f1 | UL 746C | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度抗张强度33 | |||
| 屈服Yield | 66.0 | MPa | |
| 断裂Break | 49.0 | MPa | |
| 拉伸应变伸长率33 | |||
| 屈服Yield | 8.0 | % | |
| 断裂Break | 17 | % | |
| 弯曲模量弯曲模量4 | |||
| 100 mm跨距100 mm 跨距4 | 2490 | MPa | ASTM D790 |
| 弯曲强度弯曲强度4 | |||
| 屈服，100 mm跨度屈服，100 mm 跨距4 | 99.0 | MPa | ASTM D790 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| -30℃-30°C | 96 | J/m | |
| 23℃23°C | 190 | J/m | |
| 悬臂梁缺口冲击强度悬臂梁缺口冲击强度 | |||
| 3.2mm3.20 mm | 890 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击Instrumented Dart Impact | |||
| -30℃，Energy at Peak-30°C, Energy at Peak | 11.0 | J | |
| 23℃，Energy at Peak23°C, Energy at Peak | 39.0 | J | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | |||
| 0.45 MPa，未退火，6.4 mm66 psi, Unannealed, 0.252 in | 109 | ℃ | |
| 1.8 MPa，未退火，6.4 mm264 psi, Unannealed, 0.252 in | 99.0 | ℃ | |
| 维卡软化温度Vicat Softening Temperature | 128 | ℃ | ASTM D1525 5 |
| 相对温度指数RTI | 95.0 | ℃ | UL 746 |
| 电气性能电气性能 | 95.0 | ℃ | UL 746 |
| 冲击机械性能冲击机械性能 | 80.0 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| 体积电阻率Volume Resistivity | 2.8E+16 | ohms·cm | ASTM D257 |
| 介电强度介电强度 | |||
| 3.2 mm，在油中3.20 mm，在油中 | 16 | kV/mm | ASTM D149 |
| 介电常数Dielectric Constant | |||
| 60 Hz60 Hz | 2.69 | ||
| 50 kHz50 kHz | 2.69 | ||
| 1 MHz1 MHz | 2.55 | ||
| 耗散因数Dissipation Factor | |||
| 50 Hz50 Hz | 0.010 | ||
| 60 Hz60 Hz | 0.010 | ||
| 1 MHz1 MHz | 7.0E-3 | ||
| 耐电弧性耐电弧性66 | PLC 6 | ASTM D495 | |
| 相比漏电起痕指数Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| 高电弧燃烧指数（HAI）高电弧燃烧指数(HAI)77 | PLC 0 | UL 746 | |
| 高电压电弧起痕速率高电压电弧起痕速率 | |||
| HVTRHVTR | PLC 4 | UL 746 | |
| 热丝引燃热丝引燃 | |||
| HWIHWI | PLC 1 | UL 746 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | |||
| 0.40 mm0.40 mm | HB | ||
| 1.50 mm1.5 mm | V-0 | ||
| 3.00 mm3.0 mm | 5VA | ||
| 辐射板 ListingRadiant Panel Listing88 | TRUE | ||