抗紫外线 POM 泰科纳 C 52021 高耐化学填充级注塑级|价格|厂家|多少钱-全球塑胶网-移动端

牌号简介About
符合ISO 1043-1的化学缩写：POM成型化合物ISO 9988-POM-K，M-GNR，06-002 POM共聚物极易流动的注射成型类型，适用于具有不利流动路径壁厚关系的薄壁精密成型零件；允许在低温和较短循环时间下加工；适用于机械较低的Re要求：对溶剂、燃料和强碱具有良好的耐化学性，以及良好的抗水解性；对热降解和氧化降解具有较高的抵抗力。根据21 CFR 177.2470，单体和添加剂在欧盟法规（欧盟）10/2011 FDA中列出，符合21 CFR 177.2470，天然A厚度大于0.81 mm，黑色A厚度大于1.5 mm，符合UL 94 HB，温度指数为UL 746 B，厚度为1.5 mm，电气105°C，机械90°C燃烧率为ISO 3795和FMVSS 30275 mm。/min，厚度大于1 mm。适用范围：适用于具有不利流动路径壁厚关系的非常薄壁精密模制品；允许在较低温度和较短循环时间下加工。FDA=食品药品监督管理局（美国）fmvss=联邦机动车安全标准（美国）ul=保险商实验室（美国） Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 06-002 POM copolymer Extremely easy flowing Injection molding type for very thin-walled precision molded parts with unfavourite flow-path-wallthickness relation; permits processing at reduced temperature and also shorter cycle times; for mechanical lower requirements; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 UL-registration in natural a thickness more than 0.81 mm, in black a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B for a thickness of 1.5 mm, electrical 105 °C, mechanical 90 °C Burning rate ISO 3795 and FMVSS 302 75 mm/min for a thickness more than 1 mm. Ranges of applications: For very thin- walled precision molded parts with unfavourite flow-path-wallthickness relation; permits processing at reduced temperature and also shorter cycle times. FDA = Food and Drug Administration (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA)

牌号简介About

符合ISO 1043-1的化学缩写：POM成型化合物ISO 9988-POM-K，M-GNR，06-002 POM共聚物极易流动的注射成型类型，适用于具有不利流动路径壁厚关系的薄壁精密成型零件；允许在低温和较短循环时间下加工；适用于机械较低的Re要求：对溶剂、燃料和强碱具有良好的耐化学性，以及良好的抗水解性；对热降解和氧化降解具有较高的抵抗力。根据21 CFR 177.2470，单体和添加剂在欧盟法规（欧盟）10/2011 FDA中列出，符合21 CFR 177.2470，天然A厚度大于0.81 mm，黑色A厚度大于1.5 mm，符合UL 94 HB，温度指数为UL 746 B，厚度为1.5 mm，电气105°C，机械90°C燃烧率为ISO 3795和FMVSS 30275 mm。/min，厚度大于1 mm。适用范围：适用于具有不利流动路径壁厚关系的非常薄壁精密模制品；允许在较低温度和较短循环时间下加工。FDA=食品药品监督管理局（美国）fmvss=联邦机动车安全标准（美国）ul=保险商实验室（美国） Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 06-002 POM copolymer Extremely easy flowing Injection molding type for very thin-walled precision molded parts with unfavourite flow-path-wallthickness relation; permits processing at reduced temperature and also shorter cycle times; for mechanical lower requirements; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 UL-registration in natural a thickness more than 0.81 mm, in black a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B for a thickness of 1.5 mm, electrical 105 °C, mechanical 90 °C Burning rate ISO 3795 and FMVSS 302 75 mm/min for a thickness more than 1 mm. Ranges of applications: For very thin- walled precision molded parts with unfavourite flow-path-wallthickness relation; permits processing at reduced temperature and also shorter cycle times. FDA = Food and Drug Administration (USA) FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA)

产品描述Product Description

厂家：美国塞拉尼斯Celanese EVA Performance Polymers

类别：POM共聚Copolymer Polyformaldehyde

用途：薄壁部件;

加工条件：注射成型Injection Molding

性能特点：防火阻燃等级HB; 成型周期快; 耐化学性; 耐水解; 流动性高; 耐燃油; 耐碱;Alkali resistant,High liquidity,Hydrolysis stability,Quick molding cycle,Solvent resistance,Fuel resistance,HB

技术参数Technical Data
机械性能	额定值Nominal Value	单位Units	测试方法Test Method
拉伸模量Tensile Modulus	3000	MPa	ISO 527-2/1A/1
拉伸强度拉伸强度
屈服屈服	65.0	MPa	ISO 527-2/1A/50
拉伸应变拉伸应变
屈服屈服	7.0	%	ISO 527-2/1A/50
标称拉伸断裂应变Nominal Tensile Strain at Break	15	%	ISO 527-2/1A/50
Tensile Creep Modulus（1 hr）Tensile Creep Modulus (1 hr)	2500	MPa	ISO 899-1
拉伸蠕变模量拉伸蠕变模量
1000 hr1000 hr	1300	MPa	ISO 899-1
弯曲模量弯曲模量
23℃23℃	2800	MPa	ISO 178
冲击性能	额定值Nominal Value	单位Units	测试方法Test Method
简支梁缺口冲击强度Charpy Notched Impact Strength			ISO 179/1eA
-30℃-30°C	5.0	kJ/m2	ISO 179/1eA
23℃23°C	5.0	kJ/m2	ISO 179/1eA
简支梁无缺口冲击强度Charpy Unnotched Impact Strength			ISO 179/1eU
-30℃-30°C	100	kJ/m2	ISO 179/1eU
23℃23°C	100	kJ/m2	ISO 179/1eU
热性能	额定值Nominal Value	单位Units	测试方法Test Method
热变形温度热变形温度
1.8 MPa，未退火1.8 MPa，未退火	106	℃	ISO 75-2/A
熔融温度Melting Temperature 22	166	℃	ISO 11357-3
线性热膨胀系数线性热膨胀系数
MDMD	1.1E-4	1/℃	ISO 11359-2
电气性能	额定值Nominal Value	单位Units	测试方法Test Method
表面电阻率Surface Resistivity	1.0E+14	ohms	IEC 60093
体积电阻率Volume Resistivity	1.0E+14	ohms·cm	IEC 60093
介电强度Electric Strength	35	kV/mm	IEC 60243-1
相对电容率Relative Permittivity			IEC 60250
100 Hz100 Hz	4.00		IEC 60250
1 MHz1 MHz	4.00		IEC 60250
耗散因数Dissipation Factor			IEC 60250
100 Hz100 Hz	3.0E-3		IEC 60250
1 MHz1 MHz	5.0E-3		IEC 60250
相比漏电起痕指数Comparative Tracking Index	600	V	IEC 60112
阻燃性能	额定值Nominal Value	单位Units	测试方法Test Method
阻燃等级Flame Rating			UL 94
0.80 mm0.8 mm	HB		UL 94
1.50 mm1.5 mm	HB		UL 94
物理性能	额定值Nominal Value	单位Units	测试方法Test Method
密度Density	1.41	g/cm3	ISO 1183
熔体体积流动速率熔体体积流动速率
190℃，2.16 kg190℃/2.16 kg	39.0	cm3/10min	ISO 1133
收缩率Molding Shrinkage			ISO 294-4
TDAcross Flow	1.8	%	ISO 294-4
MDFlow	1.9	%	ISO 294-4
吸水率吸水率
饱和，23℃饱和，23℃	0.65	%	ISO 62
Density of MeltDensity of Melt	1.200	g/cm3	Internal Method
Specific Heat Capacity of MeltSpecific Heat Capacity of Melt	2060	J/kg/℃	Internal Method
Thermal Conductivity of MeltThermal Conductivity of Melt	0.19	W/m/K	Internal Method