PPA HTN FR52G30BL NC010中英文物性表:
|
DuPont Zytel? HTN FR52G30BL NC010（聚酰胺-尼龙6）
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.62g/cc
|
0.0585lb/in3
|
DAM; ISO 1183
|
|
Filler Content填料含量
|
30 %
|
30 %
|
DAM
|
|
Linear Mold Shrinkage线性收缩率
|
0.0020cm/cm @Thickness 1.60 mm |
0.0020in/in @Thickness 0.0630 in |
Flow; DAM
|
|
0.0090cm/cm @Thickness 1.60 mm |
0.0090in/in @Thickness 0.0630 in |
Transverse; DAM
|
|
|
Linear Mold Shrinkage, Flow线性收缩率/流动
|
0.0030cm/cm @Thickness 2.00 mm |
0.0030in/in @Thickness 0.0787 in |
Parallel; DAM; ISO 294-4
|
|
Linear Mold Shrinkage, Transverse线性收缩率/横向
|
0.0080cm/cm @Thickness 2.00 mm |
0.0080in/in @Thickness 0.0787 in |
Normal; DAM; ISO 294-4
|
|
Melt Index of Compound熔体流动速率
|
26g/10 min @Load 2.16 kg, Temperature 325 °C |
26g/10 min @Load 4.76 lb, Temperature 617 °F |
DAM; cm3/10 min; ISO 1133
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Strength at Break断裂拉伸强度
|
150MPa @Temperature 23.0 °C |
21800psi @Temperature 73.4 °F |
50%RH; ISO 527
|
|
170MPa @Temperature 23.0 °C |
24700psi @Temperature 73.4 °F |
DAM; ISO 527
|
|
|
Tensile Strength拉伸强度
|
172MPa @Temperature 23.0 °C |
24900psi @Temperature 73.4 °F |
DAM; ASTM D638
|
|
Tensile Stress拉伸应力
|
0.000MPa @Strain 0.000 %, Temperature -20.0 °C |
0.000psi @Strain 0.000 %, Temperature -4.00 °F |
DAM; ISO 11403-1/-2
|
|
19.83MPa @Strain 0.320 %, Temperature 120 °C |
2876psi @Strain 0.320 %, Temperature 248 °F |
50%RH; ISO 11403-1/-2
|
|
|
78.74MPa @Strain 0.920 %, Temperature 40.0 °C |
11420psi @Strain 0.920 %, Temperature 104 °F |
50%RH; ISO 11403-1/-2
|
|
|
119.91MPa @Strain 1.84 %, Temperature 40.0 °C |
17392psi @Strain 1.84 %, Temperature 104 °F |
50%RH; ISO 11403-1/-2
|
|
|
157.6MPa @Strain 1.80 %, Temperature 40.0 °C |
22860psi @Strain 1.80 %, Temperature 104 °F |
DAM; ISO 11403-1/-2
|
|
|
188.54MPa @Strain 2.00 %, Temperature -20.0 °C |
27345psi @Strain 2.00 %, Temperature -4.00 °F |
DAM; ISO 11403-1/-2
|
|
|
Elongation at Break断裂伸长率
|
2.0 % @Temperature 23.0 °C |
2.0 % @Temperature 73.4 °F |
DAM; ISO 527
|