江苏普及塑料有限公司
| 牌号简介About |
|---|
| Tenac?-C CF454是一种聚甲醛（POM）共聚物产品,含有的填充物为碳纤维增强材料。 它,在北美洲、非洲和中东、欧洲或亚太地区有供货。 Tenac?-C CF454的应用领域包括工程/工业配件 和 房屋。 特性包括: 阻燃/额定火焰 传导性 高刚度 高强度 共聚物 Tenac?-C CF454 is an Acetal (POM) Copolymer product filled with carbon fiber. It is available in Africa Middle East, Asia Pacific, Europe, or North America. Applications of Tenac?-C CF454 include engineering/industrial parts and housings. Characteristics include: Flame Rated Conductive Copolymer High Stiffness High Strength |
产品描述Product Description
厂家：日本旭化成Asahi Kasei Corporation
类别：POM共聚Copolymer Polyformaldehyde
用途：工程配件;齿轮;外壳;
性能特点：防火阻燃等级HB; 机械强度好; 导电; 共聚物;Good Rigidity,Conductive,Copolymer,HB
填料：碳纤维
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.46 | g/cm3 | ASTM D792 , ISO 1183 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 190℃，2.16kg190℃/2.16 kg | 4.0 | g/10min | ISO 1133 |
| 收缩率Molding Shrinkage | 内部方法 | ||
| MD流动 | 0.10 到 0.20 | % | 内部方法 |
| TD横向流动 | 0.60 到 0.80 | % | 内部方法 |
| 吸水率吸水率 | |||
| 23℃，24hr，50% RH23℃，24 hr，50% RH | 0.20 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | 5.0 | kJ/m2 | ISO 179 |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | 39 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | |||
| 0.45 MPa，未退火66 psi, Unannealed | 166 | ℃ | ASTM D648，ISO 75-2/B |
| 1.8 MPa，未退火264 psi, Unannealed | 163 | ℃ | ASTM D648，ISO 75-2/A |
| 线性热膨胀系数CLTE | |||
| MD流动 | 4.0E-5 | 1/℃ | ASTM D696 |
| MD流动 | 4.0E-5 到 9.0E-5 | 1/℃ | ISO 11359-2 |
| TDTransverse | 9.0E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级0.75 mm | |||
| 0.75 mm | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度洛氏硬度 | |||
| M 级M 级 | 104 | ASTM D785 | |
| 拉伸模量Tensile Modulus | 13000 | MPa | ISO 527-2 |
| 拉伸强度Tensile Stress | |||
| 断裂Break | 130 | MPa | ISO 527-2 |
| ---- | 118 | MPa | ASTM D638 |
| 拉伸应变Tensile Elongation | |||
| 断裂Break | 5.0 | % | ASTM D638 |
| 断裂Break | 1.0 | % | ISO 527-2 |
| 弯曲模量Flexural Modulus | |||
| ---- | 12200 | MPa | ASTM D790 |
| ---- | 12500 | MPa | ISO 178 |
| 弯曲强度Flexural Strength | 185 | MPa | ASTM D790 |