江苏普及塑料有限公司
| 牌号简介About |
|---|
| Tenac?-C 4513是一种聚甲醛（POM）共聚物产品,。 它,在北美洲、非洲和中东、欧洲或亚太地区有供货。 Tenac?-C 4513的应用领域包括工程/工业配件、房屋 和 汽车行业。 特性包括: 共聚物 良好的抗紫外线能力 耐候性好 中等粘度 Tenac?-C 4513 is an Acetal (POM) Copolymer product. It is available in Africa Middle East, Asia Pacific, Europe, or North America. Applications of Tenac?-C 4513 include engineering/industrial parts, automotive and housings. Characteristics include: Copolymer Medium Viscosity UV Resistant Weather Resistant |
产品描述Product Description
厂家：日本旭化成Asahi Kasei Corporation
类别：POM共聚Copolymer Polyformaldehyde
用途：工程配件;齿轮;外壳;汽车内部零件;
性能特点：共聚物; 耐候抗UV;Weather resistance is good,Copolymer
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.41 | g/cm3 | ASTM D792 , ISO 1183 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 190℃，2.16kg190℃/2.16 kg | 9.0 | g/10min | ISO 1133 |
| 收缩率收缩率 | |||
| MDMD | 1.6 到 2.0 | % | 内部方法 |
| 吸水率吸水率 | |||
| 23℃，24hr，50% RH23℃，24 hr，50% RH | 0.20 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | 7.0 | kJ/m2 | ISO 179 |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | 60 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | |||
| 0.45 MPa，未退火66 psi, Unannealed | 158 | ℃ | ASTM D648 |
| 0.45 MPa，未退火66 psi, Unannealed | 154 | ℃ | ISO 75-2/B |
| 1.8 MPa，未退火264 psi, Unannealed | 110 | ℃ | ASTM D648 |
| 1.8 MPa，未退火264 psi, Unannealed | 97.0 | ℃ | ISO 75-2/A |
| 线性热膨胀系数线性热膨胀系数 | |||
| MDMD | 1.0E-4 | 1/℃ | ASTM D696，ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+16 到 1.0E+17 | ohms | ASTM D257 |
| 体积电阻率体积电阻率 | |||
| 23℃23℃ | 1.0E+15 到 1.0E+16 | ohms·cm | ASTM D257 |
| 介电强度Electric Strength | 19 | kV/mm | ASTM D149 |
| 耐电弧性Arc Resistance | 250 | sec | ASTM D495 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度Rockwell Hardness | ASTM D785 | ||
| M 级M 级 | 80 | ASTM D785 | |
| R 级R 级 | 115 | ASTM D785 | |
| 拉伸模量Tensile Modulus | 2550 | MPa | ISO 527-2 |
| 拉伸强度Tensile Stress | |||
| 屈服Yield | 63.0 | MPa | ISO 527-2 |
| ---- | 62.0 | MPa | ASTM D638 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 35 | % | ASTM D638 , ISO 527-2 |
| 弯曲模量Flexural Modulus | |||
| ---- | 2500 | MPa | ASTM D790 |
| ---- | 2450 | MPa | ISO 178 |
| 弯曲强度Flexural Strength | 88.0 | MPa | ASTM D790 |
| 泰伯耐磨性Taber Abrasion Resistance | 14.0 | mg | ASTM D1044 |