POM CELCON M15HP
Celcon? acetal copolymer grade M15HP is a creep resistant, high viscosity polymer
Standard extruders with a length to diameter ratio of at least 20:1 are recommended. The screw should be a high compression ratio of at least 3:1 and preferably 4:1 to assure good melting and melt homogeneity. The design should be approximately 35% each f
Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (i.e.-general purpose with a 2:1 compression ratio) c
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.41g/cc | 1.41g/cc | ASTM D792 |
Density | 1.41g/cc | 0.0509lb/in3 | ISO 1183 |
Density of Compound | 1.165g/cc | 0.04209lb/in3 | |
Moisture Absorption | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 |
Water Absorption at Saturation | 0.750 % | 0.750 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.0230cm/cm | 0.0230in/in | ISO 294-4 |
Linear Mold Shrinkage, Transverse | 0.0190cm/cm | 0.0190in/in | ISO 294-4 |
Melt Flow | 1.50g/10 min | 1.50g/10 min | ASTM D1238 |
1.30g/10 min
@Load 2.16 kg, Temperature 190 °C |
1.30g/10 min
@Load 4.76 lb, Temperature 374 °F |
[cm3/10min]; ISO 1133 |
POM CELCON M15HP
特点
(1)POM加工前可不用干燥,最好在加工过程中进行预热(80℃左右),对产品尺寸的稳定性有好处.
(2) POM的加工温度很窄(0~215℃),在炮筒内停留时间稍长或温度超过220℃时就会分解,产生刺激性强的甲醛气体.
(3) POM料注塑时保压压力要较大(与注射压力相近),以减少压力降.螺杆转速不能过高,残量要少;
(4) POM产品收缩率较大,易产生缩水或变形.POM比热大,模温高(80~100℃),产品脱模时很烫,需防止烫伤手指.
(5) POM宜在“中压、中速、低料温、较高模温”的条件下成型加工,精密制品成型时需用控制模温
(6)具高机械强度和刚性
(7)最高的疲劳强度
(8)环境抵抗性、耐有机溶剂性佳
(9)耐反覆冲击性强,良好的电气性质,复原性良好,具自已润滑性、耐磨性良好,尺寸安定性优.
应用
.可代替大部分有色金属、汽车、机床、仪表内件、轴承、紧固件、齿轮、弹簧片、管道、运输带配件、电水煲、泵壳、沥水器、水龙头等.