江苏普及塑料有限公司
| 牌号简介About |
|---|
| Iupital? FL2010是一种聚甲醛（POM）共聚物材料,。 该产品在亚太地区、北美洲或欧洲有供货,加工方式为:注射成型。 Iupital? FL2010的主要特性有: 阻燃/额定火焰 润滑 耐磨 Iupital? FL2010 is an Acetal (POM) Copolymer material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupital? FL2010 are: Flame Rated Lubricated Wear Resistant |
产品描述Product Description
厂家：日本三菱Mitsubishi Chemical Corporation
类别：POM共聚Copolymer Polyformaldehyde
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级HB; 耐磨; 低摩擦系数;Low coefficient of friction,Good wear resistance,HB
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.46 | g/cm3 | ISO 1183 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 190℃，2.16kg190℃/2.16 kg | 7.5 | g/10min | ISO 1133 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 190℃，2.16 kg190℃/2.16 kg | 6.10 | cm3/10min | ISO 1133 |
| 收缩率收缩率 | |||
| MD：3.0 mmMD，3.00 mm | 2.0 | % | |
| 吸水率吸水率1 | |||
| 平衡，23℃，50% RH平衡，23℃，50% RH1 | 0.19 | % | ISO 62 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 2650 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |||
| 屈服屈服 | 52.0 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 屈服屈服 | 8.0 | % | ISO 527-2 |
| 标称拉伸断裂应变Nominal Tensile Strain at Break | 18 | % | ISO 527-2 |
| 弯曲模量Flexural Modulus | 2400 | MPa | ISO 178 |
| 弯曲强度Flexural Stress | 77.0 | MPa | ISO 178 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度简支梁缺口冲击强度 | |||
| 23℃23℃ | 5.0 | kJ/m2 | ISO 179 |
| 简支梁无缺口冲击强度简支梁无缺口冲击强度 | |||
| 23℃23℃ | 60 | kJ/m2 | ISO 179 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Heat Deflection Temperature | |||
| 0.45 MPa，未退火66 psi, Unannealed | 154 | ℃ | ISO 75-2/B |
| 1.8 MPa，未退火264 psi, Unannealed | 97.0 | ℃ | ISO 75-2/A |
| 熔融温度Melting Temperature | 166 | ℃ | ISO 11357-3 |
| 线性热膨胀系数CLTE | ISO 11359-2 | ||
| MD流动 | 1.1E-4 | 1/℃ | |
| TDTransverse | 1.1E-4 | 1/℃ | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| 体积电阻率Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| 介电强度Electric Strength | IEC 60243-1 | ||
| 1 mm1.00 mm | 25 | kV/mm | |
| 3 mm3.00 mm | 16 | kV/mm | |
| 相比漏电起痕指数Comparative Tracking Index | 600 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 0.80 mm0.800 mm | HB | UL 94 | |