BASF Ultramid? A3K PA66 (尼龙66-聚酰胺)
The property table is provided bywww.plas-cn.com, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
1.13g/cc
|
0.0408lb/in3
|
ISO 1183
|
|
Water Absorption吸水率
|
8.0 - 9.0 %
|
8.0 - 9.0 %
|
ISO 62
|
|
Moisture Absorption at Equilibrium吸湿平衡
|
2.5 - 3.1 %
|
2.5 - 3.1 %
|
23°C/50% R.H.; ISO 62
|
|
Viscosity Measurement粘度
|
150
|
150
|
Viscosity number; ISO 307
|
|
Linear Mold Shrinkage线性收缩率
|
0.0085cm/cm
|
0.0085in/in
|
|
|
Melt Flow熔体流动速率
|
129.95g/10 min@Load 5.00 kg,Temperature 275 °C
|
129.95g/10 min@Load 11.0 lb,Temperature 527 °F
|
ISO 1133
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Tensile Strength, Yield屈服拉伸强度
|
85.0MPa
|
12300psi
|
50mm/min; ISO 527
|
|
Elongation at Yield屈服伸长率
|
5.0 %
|
5.0 %
|
50mm/min; ISO 527
|
|
Modulus of Elasticity弹性模量
|
3.10GPa
|
450ksi
|
ISO 527
|
|
Flexural Modulus弯曲弹性模量
|
2.90GPa
|
421ksi
|
ISO 178
|
|
Izod Impact, Notched悬臂梁缺口冲击强度(ISO)
|
5.50kJ/m2
|
2.62ft-lb/in2
|
ISO 180/A
|
|
6.00kJ/m2@Temperature -30.0 °C
|
2.86ft-lb/in2@Temperature -22.0 °F
|
ISO 180/A
|
|
|
Charpy Impact Unnotched夏比缺口试样冲击
|
NB
|
NB
|
ISO 179/1eU
|
|
Charpy ImPAct, Notched夏比缺口冲击
|
0.500J/cm2
|
2.38ft-lb/in2
|
ISO 179/1eA
|
|
0.400J/cm2@Temperature -30.0 °C
|
1.90ft-lb/in2@Temperature -22.0 °F
|
ISO 179/1eA
|
|
|
Electrical Properties电性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Volume ResiSTivity体积电阻率
|
1.00e 13ohm-cm
|
1.00e 13ohm-cm
|
IEC 60093
|
|
Dielectric Constant介电常数
|
3.2@Frequency 1.00e 6 Hz
|
3.2@Frequency 1.00e 6 Hz
|
IEC 60250
|
|
Dissipation Factor耗散因数
|
0.025@Frequency 1.00e 6 Hz
|
0.025@Frequency 1.00e 6 Hz
|
IEC 60250
|
|
Comparative Tracking Index跟踪指数
|
600V
|
600V
|
Test Solution A; IEC 60112
|
|
Thermal Properties热性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
CTE, linear, Parallel to Flow线性热膨胀系数
|
0.700-1.00μm/m-°C@Temperature 23.0 - 80.0 °C
|
0.389-0.556μin/in-°F@Temperature 73.4 - 176 °F
|
ISO 11359-1/-2
|
|
Specific Heat Capacity比热容
|
1.70J/g-°C
|
0.406BTU/lb-°F
|
|
|
Thermal Conductivity导热系数
|
0.330W/m-K
|
2.29BTU-in/hr-ft2-°F
|
DIN 52612
|
|
Melting Point熔点
|
260°C
|
500°F
|
DIN 53765
|
|
Maximum Service Temperature, Air最高使用温度
|
220°C
|
428°F
|
|
|
Deflection Temperature at热变形温度0.46 MPa (66 psi)
|
220°C
|
428°F
|
ISO 75
|
|
Deflection Temperature at热变形温度1.8 MPa (264 psi)
|
75.0°C
|
167°F
|
ISO 75
|
|
Flammability, UL94阻燃等级
|
V-2@Thickness =0.400 mm
|
V-2@Thickness =0.0157 in
|
|
|
Processing Properties加工性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Melt Temperature熔体温度熔体温度
|
280-300°C
|
536-572°F
|
|
|
Mold Temperature模具温度
|
60.0-80.0°C
|
140-176°F
|
|