江苏普及塑料有限公司
| 牌号简介About |
|---|
| 有核中高粘度缩醛均聚物 Nucleated Medium-high Viscosity Acetal Homopolymer |
产品描述Product Description
厂家：美国杜邦DuPont Canada, Inc. - Dartek Division
类别：POM均聚Paraformaldehyde
加工条件：注射成型Injection Molding
性能特点：成核的; 防火阻燃等级HB;Nucleation,HB
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.42 | g/cm3 | ISO 1183 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 190℃，2.16kg190℃/2.16 kg | 7.0 | g/10min | ISO 1133 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 190℃，2.16 kg190℃/2.16 kg | 6.00 | cm3/10min | ISO 1133 |
| 收缩率Molding Shrinkage | ISO 294-4 | ||
| TDAcross Flow | 1.8 | % | ISO 294-4 |
| MDFlow | 1.9 | % | ISO 294-4 |
| 吸水率吸水率 | |||
| 饱和，23℃，2.00 mmSaturation，23℃，2.00 mm | 0.90 | % | ISO 62 |
| 平衡，23℃，50% RH，2.00 mmEquilibrium，23℃，2.00 mm，50% RH | 0.20 | % | ISO 62 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃-30°C | 8.0 | kJ/m2 | ISO 179/1eA |
| 23℃23°C | 9.0 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30℃-30°C | 250 | kJ/m2 | ISO 179/1eU |
| 23℃23°C | 300 | kJ/m2 | ISO 179/1eU |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | ISO 180/1A | ||
| -40℃-40°C | 8.0 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 10 | kJ/m2 | ISO 180-1A |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 103 | ℃ | ISO 75-2/A |
| 0.45 MPa，未退火0.45 MPa，未退火 | 165 | ℃ | ISO 75-2/B |
| 维卡软化温度维卡软化温度 | |||
| B50B50 | 160 | ℃ | ISO 306 |
| 熔融温度Melting Temperature 22 | 178 | ℃ | ISO 11357-3 |
| 线性热膨胀系数线性热膨胀系数 | |||
| TDTD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MDMD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| 退火温度Annealing Temperature | 160 | ℃ | |
| 退火时间退火时间 | |||
| OptionalOptional | 30.0 | min/mm | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 100 Hz100 Hz | 3.80 | IEC 60250 | |
| 1 MHz1 MHz | 3.80 | IEC 60250 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 燃烧速率燃烧速率3 | |||
| 1 mm1.00 mm3 | 100 | mm/min | ISO 3795 |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.80 mm0.8 mm | HB | UL 94 | |
| 1.50 mm1.5 mm | HB | UL 94 | |
| 可燃性等级Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.8 mm0.8 mm | HB | IEC 60695-11-10, -20 | |
| 1.5 mm1.5 mm | HB | IEC 60695-11-10, -20 | |
| FMVSS 阻燃等级FMVSS Flammability | B | FMVSS 302 | |
| Fogging（Gvalue，condensate）Fogging - G-value (condensate) | 4.0E-4 | g | ISO 6452 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 排放Emission | 8.00 | mg/kg | VDA 275 |
| 有机化合物的排放Emission of Organic Compounds | 7.30 | μgC/g | VDA 277 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 3300 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |||
| 屈服屈服 | 74.0 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 屈服屈服 | 15 | % | ISO 527-2 |
| 标称拉伸断裂应变Nominal Tensile Strain at Break | 35 | % | ISO 527-2 |
| 弯曲模量Flexural Modulus | 3100 | MPa | ISO 178 |
| 弯曲强度弯曲强度 | |||
| 3.50% 应变3.5% 应变 | 86.0 | MPa | ISO 178 |
| 洛氏硬度Rockwell Hardness | ISO 2039-2 | ||
| M 级M-Scale | 98 | ISO 2039-2 | |
| R 级R-Scale | 122 | ISO 2039-2 | |