江苏普及塑料有限公司
| 牌号简介About |
|---|
| Lexan 223R树脂17.5 mfr，用于小型复杂零件。提高了阻燃性。内部模具释放。紫外光稳定。Lexan 223R树脂Lexan 223R是一种低粘度、紫外光稳定的多用途级树脂，含有一种释放剂，以确保易于加工。该等级为UL94-V2，批准0.8 mm。 17.5 MFR, for small, intricate parts. Improved flame retardance. Internal mold release. UV stabilized. |
产品描述Product Description
厂家：沙特沙伯基础SABIC
类别：PCPolycarbonate
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级V-0; 防火阻燃等级V-2; 阻燃; 低粘度; 耐候抗UV; 易加工;Weather resistance is good,Excellent Processability,Low Viscosity,Flame Characteristics,V-2,V-0
紫外线：UV Stabilized
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.19 | g/cm3 | ASTM D792 |
| 特定体积Specific Volume | 0.830 | cm3/g | ASTM D792 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 300℃，1.20kg300℃/1.2 kg | 18 | g/10min | ASTM D1238 |
| 收缩率收缩率 | |||
| MD：3.2 mmMD，3.20 mm | 0.50 to 0.70 | % | 内部方法 |
| 吸水率Water Absorption | ASTM D570 | ||
| 24hr24 hr | 0.15 | % | ASTM D570 |
| 平衡，23℃Equilibrium, 73°F | 0.35 | % | ASTM D570 |
| 平衡，100℃Equilibrium, 212°F | 0.58 | % | ASTM D570 |
| 耐候性室外适用性/耐候等级 | f1 | UL 746C | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength 44 | ISO 179/1eA | ||
| -30℃-30°C | 12 | kJ/m2 | ISO 179/1eA |
| 23℃23°C | 65 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength 44 | ISO 179/1eU | ||
| -30℃-30°C | No Break | ISO 179/1eU | |
| 23℃23°C | No Break | ISO 179/1eU | |
| 悬臂梁缺口冲击强度Notched Izod Impact 55 | ISO 180/1A | ||
| 23℃23℃ | 690 | J/m | ASTM D256 |
| 23℃23℃ | 3200 | J/m | ASTM D4812 |
| -30℃-30°C | 11 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 65 | kJ/m2 | ISO 180-1A |
| 悬臂梁无缺口冲击强度Unnotched Izod Impact Strength 55 | ISO 180/1U | ||
| -30℃-30°C | No Break | ISO 180/1U | |
| 23℃23°C | No Break | ISO 180/1U | |
| 落锤冲击落锤冲击 | |||
| 23℃23℃ | 169 | J | ASTM D3029 |
| 拉伸冲击强度Tensile Impact Strength 66 | 546 | kJ/m2 | ASTM D1822 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火，6.4 mm1.8 MPa，未退火，6.40 mm | 132 | ℃ | ASTM D648 |
| 0.45 MPa，未退火，6.4 mm0.45 MPa，未退火，6.40 mm | 138 | ℃ | ASTM D648 |
| 维卡软化温度Vicat Softening Temperature | 154 | ℃ | ASTM D1525 7 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MD：-40~95℃MD：-40 到 95℃ | 6.8E-5 | 1/℃ | ASTM E831 |
| 比热Specific Heat | 1260 | J/kg/℃ | ASTM C351 |
| 导热系数Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| 相对温度指数相对温度指数 | |||
| 电气性能电气性能 | 100 | ℃ | UL 746 |
| 强度机械性能强度机械性能 | 100 | ℃ | UL 746 |
| 冲击机械性能冲击机械性能 | 100 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度介电强度 | |||
| 3.2 mm，在空气中3.20 mm，在空气中 | 15 | kV/mm | ASTM D149 |
| 介电常数Dielectric Constant | ASTM D150 | ||
| 50 Hz50 Hz | 3.17 | ASTM D150 | |
| 60 Hz60 Hz | 3.17 | ASTM D150 | |
| 1 MHz1 MHz | 2.96 | ASTM D150 | |
| 耗散因数Dissipation Factor | ASTM D150 | ||
| 50 Hz50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz1 MHz | 0.010 | ASTM D150 | |
| 相比漏电起痕指数Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| 高电弧燃烧指数（HAI）High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| 高电压电弧起痕速率高电压电弧起痕速率 | |||
| HVTRHVTR | PLC 2 | UL 746 | |
| 热丝引燃热丝引燃 | |||
| HWIHWI | PLC 4 | UL 746 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.75 mm0.75 mm | V-2 | UL 94 | |
| 6.00 mm6.0 mm | V-0 | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 折射率Refractive Index | 1.586 | ASTM D542 | |
| 透光率透射率 | |||
| 2540 μm2540 μm | 88.0 | % | ASTM D1003 |
| 雾度雾度 | |||
| 2540 μm2540 μm | 1.0 | % | ASTM D1003 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度2 | |||
| 断裂断裂2 | 65.5 | MPa | ASTM D638 |
| 屈服屈服2 | 62.1 | MPa | ASTM D638 |
| 拉伸应变拉伸应变2 | |||
| 断裂断裂2 | 110 | % | ASTM D638 |
| 屈服屈服2 | 7.0 | % | ASTM D638 |
| 弯曲模量弯曲模量4 | |||
| 50 mm跨距50.0 mm 跨距4 | 2340 | MPa | ASTM D790 |
| 弯曲强度弯曲强度4 | |||
| 屈服，50 mm跨度屈服，50.0 mm 跨距4 | 93.1 | MPa | ASTM D790 |
| 泰伯耐磨性泰伯耐磨性 | |||
| 1000 周期，1000 g，CS-17 转轮1000 周期，1000 g，CS-17 转轮 | 10.0 | mg | ASTM D1044 |
| 洛氏硬度Rockwell Hardness | ASTM D785 | ||
| M 级M-Scale | 70 | ASTM D785 | |
| R 级R-Scale | 118 | ASTM D785 | |