| LEXAN? 4701R resin是高耐热聚碳酸酯，LEXAN? 4701R resin是聚碳酸酯树脂的共聚物，用于需要高耐热性的应用。与Lexan 4501相比，该等级具有更高的热性能。 High heat resistant polyphthlate carbonate, provides DTUL of 300F at 264 psi. |
产品描述Product Description
厂家：沙特沙伯基础SABIC
类别：PPCPPC
加工条件：注射成型Injection Molding
性能特点：共聚物; 耐高温;High Heat Resistance,Copolymer
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.19 | g/cm3 | ASTM D792 |
| 特定体积Specific Volume | 0.830 | cm3/g | ASTM D792 |
| 熔体质量流动速率Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 300℃，1.20kg300°C/1.2 kg | 2.0 | g/10min | ASTM D1238 |
| 300℃，6.10kg300°C/6.1 kg | 9.0 | g/10min | ASTM D1238 |
| 收缩率收缩率 | |||
| MD：3.2 mmMD，3.20 mm | 0.80 to 1.0 | % | 内部方法 |
| 吸水率吸水率 | |||
| 24hr24 hr | 0.19 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度 | |||
| 23℃23℃ | 3200 | J/m | ASTM D4812 |
| 23℃23℃ | 370 | J/m | ASTM D256 |
| 落锤冲击落锤冲击 | |||
| 23℃23℃ | 149 | J | ASTM D3029 |
| 拉伸冲击强度Tensile Impact Strength 44 | 578 | kJ/m2 | ASTM D1822 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火，3.2 mm1.8 MPa，未退火，3.20 mm | 149 | ℃ | ASTM D648 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MD：-40~95℃MD：-40 到 95℃ | 8.1E-5 | 1/℃ | ASTM E831 |
| 比热Specific Heat | 1260 | J/kg/℃ | ASTM C351 |
| 导热系数Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| 相对温度指数相对温度指数 | |||
| 电气性能电气性能 | 130 | ℃ | UL 746 |
| 强度机械性能强度机械性能 | 130 | ℃ | UL 746 |
| 冲击机械性能冲击机械性能 | 130 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 2.5E+17 | ohms·cm | ASTM D257 |
| 介电强度介电强度 | |||
| 3.2 mm，在空气中3.20 mm，在空气中 | 20 | kV/mm | ASTM D149 |
| 介电常数Dielectric Constant | ASTM D150 | ||
| 50 Hz50 Hz | 3.27 | ASTM D150 | |
| 60 Hz60 Hz | 3.27 | ASTM D150 | |
| 1 MHz1 MHz | 3.10 | ASTM D150 | |
| 耗散因数Dissipation Factor | ASTM D150 | ||
| 50 Hz50 Hz | 1.6E-3 | ASTM D150 | |
| 60 Hz60 Hz | 1.6E-3 | ASTM D150 | |
| 100 Hz100 Hz | 0.026 | ASTM D150 | |
| 耐电弧性Arc Resistance 55 | PLC 6 | ASTM D495 | |
| 相比漏电起痕指数Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| 高电弧燃烧指数（HAI）High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| 高电压电弧起痕速率高电压电弧起痕速率 | |||
| HVTRHVTR | PLC 3 | UL 746 | |
| 热丝引燃热丝引燃 | |||
| HWIHWI | PLC 2 | UL 746 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 折射率Refractive Index | 1.600 | ASTM D542 | |
| 透光率透射率 | |||
| 2540 μm2540 μm | 85.0 | % | ASTM D1003 |
| 雾度雾度 | |||
| 2540 μm2540 μm | 1.0 | % | ASTM D1003 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度2 | |||
| 断裂断裂2 | 77.9 | MPa | ASTM D638 |
| 屈服屈服2 | 65.5 | MPa | ASTM D638 |
| 拉伸应变拉伸应变2 | |||
| 断裂断裂2 | 78 | % | ASTM D638 |
| 弯曲模量弯曲模量4 | |||
| 50 mm跨距50.0 mm 跨距4 | 2330 | MPa | ASTM D790 |
| 弯曲强度弯曲强度4 | |||
| 屈服，50 mm跨度屈服，50.0 mm 跨距4 | 97.2 | MPa | ASTM D790 |
| 洛氏硬度Rockwell Hardness | ASTM D785 | ||
| M 级M-Scale | 92 | ASTM D785 | |
| R 级R-Scale | 127 | ASTM D785 | |