江苏普及塑料有限公司
| 牌号简介About |
|---|
| MVR（300°C/1.2 kg）8.0 cm3/10 min；20%玻璃纤维增强；阻燃；UL 94V-0/1.5 mm；中等粘度；易释放；注射成型-熔融温度310-330°C；仅提供不透明颜色 MVR (300 °C/1.2 kg) 8.0 cm3/10 min; 20 % glass fiber reinforced; flame retardant; UL 94V-0/1.5 mm; medium viscosity; easy release; injection molding - melt temperature 310 - 330 °C; available in opaque colors only |
产品描述Product Description
厂家：德国科思创Covestro - PUR
类别：PCPolycarbonate
颜色：可用颜色,不透明
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级V-0; 含脱模剂; 防火阻燃等级V-2; 阻燃;Good stripping performance,Flame Characteristics,V-2,V-0
填料：玻璃纤维 20
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density (73°F) | 1.34 | g/cm3 | ISO 1183 |
| 表观密度Apparent Density 22 | 0.64 | g/cm3 | ISO 60 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 300℃，1.20kg300℃/1.2 kg | 10 | g/10min | ISO 1133 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 300℃，1.2 kg300℃/1.2 kg | 8.00 | cm3/10min | ISO 1133 |
| 收缩率Molding Shrinkage | |||
| TDAcross Flow | 0.30 to 0.50 | % | ISO 2577 |
| MDFlow | 0.30 to 0.50 | % | ISO 2577 |
| TD：2.0 mmAcross Flow : 0.0787 in 33 | 0.45 | % | ISO 294-4 |
| MD：2.0 mmFlow : 0.0787 in 33 | 0.35 | % | ISO 294-4 |
| 吸水率吸水率 | |||
| 饱和，23℃饱和，23℃ | 0.24 | % | ISO 62 |
| 平衡，23℃，50% RH平衡，23℃，50% RH | 0.10 | % | ISO 62 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度简支梁缺口冲击强度6 | |||
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30℃，完全断裂-22°F, Complete Break | 45 | kJ/m2 | ISO 179/1eU |
| 23℃，完全断裂73°F, Complete Break | 40 | kJ/m2 | ISO 179/1eU |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度7 | |||
| 23℃，完全断裂23℃，完全断裂7 | 8.0 | kJ/m2 | ISO 7391 |
| 多轴向仪器化冲击能量Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -30℃-30°C | 5.00 | J | ISO 6603-2 |
| 23℃23°C | 5.00 | J | ISO 6603-2 |
| 多轴向仪器化冲击力峰值Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | ||
| -30℃-30°C | 800 | N | ISO 6603-2 |
| 23℃23°C | 800 | N | ISO 6603-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 138 | ℃ | ISO 75-2/A |
| 0.45 MPa，未退火0.45 MPa，未退火 | 142 | ℃ | ISO 75-2/B |
| 维卡软化温度Vicat Softening Temperature | |||
| B50-- | 145 | ℃ | ISO 306 |
| B120-- | 146 | ℃ | ISO 306/B120 |
| 球压测试球压测试 | |||
| 136℃136℃ | Pass | IEC 60695-10-2 | |
| 线性热膨胀系数线性热膨胀系数 | |||
| TD：23~55℃TD：23 到 55℃ | 6.5E-5 | 1/℃ | ISO 11359-2 |
| MD：23~55℃MD：23 到 55℃ | 3.0E-5 | 1/℃ | ISO 11359-2 |
| 导热系数导热系数8 | |||
| 23℃23℃8 | 0.23 | W/m/K | ISO 8302 |
| 相对温度指数相对温度指数 | |||
| 电气性能，1.50 mm电气性能，1.5 mm | 130 | ℃ | UL 746 |
| 强度机械性能，1.50 mm强度机械性能，1.5 mm | 125 | ℃ | UL 746 |
| 冲击机械性能，1.50 mm冲击机械性能，1.5 mm | 125 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| 体积电阻率体积电阻率 | |||
| 23℃23℃ | 1.0E+16 | ohms·cm | IEC 60093 |
| 介电强度介电强度 | |||
| 23 ℃，1 mm23℃，1.00 mm | 36 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 23℃，100 Hz23°C, 100 Hz | 3.30 | IEC 60250 | |
| 23℃，1 MHz23°C, 1 MHz | 3.30 | IEC 60250 | |
| 耗散因数Dissipation Factor | IEC 60250 | ||
| 23℃，100 Hz23°C, 100 Hz | 1.0E-3 | IEC 60250 | |
| 23℃，1 MHz23°C, 1 MHz | 9.0E-3 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | IEC 60112 | ||
| 解决方案 ASolution A | 175 | V | IEC 60112 |
| 解决方案 BSolution B | 125 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.36 mm0.36 mm | V-2 | UL 94 | |
| 1.50 mm1.5 mm | V-0 | UL 94 | |
| 灼热丝可燃性指数Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.5 mm1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| 灼热丝起燃温度Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.5 mm1.5 mm | 850 | ℃ | IEC 60695-2-13 |
| 3 mm3.0 mm | 850 | ℃ | IEC 60695-2-13 |
| 极限氧指数Oxygen Index 99 | 35 | % | ISO 4589-2 |
| 小型燃烧器火焰的应用Application of Flame from Small Burner | |||
| 2.00 mm2.00 mm | B2 | DIN 4102 | |
| Method K and F：2.00 mmMethod K and F : 2.00 mm | K1, F1 | DIN 53438-1, -3 | |
| 燃烧速率燃烧速率 | |||
| USFMVSS， 1.00 mmUSFMVSS， 1.00 mm | passed | ISO 3795 | |
| Flash Ignition TemperatureFlash Ignition Temperature | 470 | ℃ | ASTM D1929 |
| 针焰测试Needle Flame Test | IEC 60695-11-5 | ||
| Method F：1.50 mmMethod F : 1.50 mm | 2.0 | min | IEC 60695-11-5 |
| Method F：2.00 mmMethod F : 2.00 mm | 2.0 | min | IEC 60695-11-5 |
| Method F：3.00 mmMethod F : 3.00 mm | 2.0 | min | IEC 60695-11-5 |
| Method K：1.50 mmMethod K : 1.50 mm | 1.0 | min | IEC 60695-11-5 |
| Method K：2.00 mmMethod K : 2.00 mm | 2.0 | min | IEC 60695-11-5 |
| Method K：3.00 mmMethod K : 3.00 mm | 2.0 | min | IEC 60695-11-5 |
| 自燃温度Self Ignition Temperature | 550 | ℃ | ASTM D1929 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 电解腐蚀电解腐蚀 | |||
| 23℃23℃ | A1 | IEC 60426 | |
| ISO ShortnameISO Shortname | ISO 7391-PC,MFR,(,,)-09-3,GF20 | ||
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量拉伸模量 | |||
| 23℃23℃ | 5800 | MPa | ISO 527-1-2 |
| 拉伸强度拉伸强度 | |||
| 断裂，23℃断裂，23℃ | 85.0 | MPa | ISO 527-2/5 |
| 拉伸应变拉伸应变 | |||
| 断裂，23℃断裂，23℃ | 2.5 | % | ISO 527-2/5 |
| Tensile Creep Modulus（1 hr）Tensile Creep Modulus (1 hr) | 5700 | MPa | ISO 899-1 |
| 拉伸蠕变模量拉伸蠕变模量 | |||
| 1000 hr1000 hr | 5200 | MPa | ISO 899-1 |
| 弯曲模量弯曲模量4 | |||
| 23℃23℃4 | 5600 | MPa | ISO 178 |
| 弯曲强度弯曲强度4 | |||
| 23℃23℃4 | 140 | MPa | ISO 178 |
| 弯曲应变Flexural Strain at Flexural Strength 5 (23°C)5 | 3.0 | % | ISO 178 |
| 球压硬度Ball Indentation Hardness | 148 | MPa | ISO 2039-1 |