韩国LG ABS AF312B

Feature: Injection Molding, Flame Retardant

Application: Electric/Electronic Applications (TV, Monitor Housing) IT/OA device

CAS No. 9003-56-9, 79-94-7 and 1309-64-4

Information provided by LG Chemical

Physical Properties	Metric	English	Comments
Specific Gravity	1.18g/cc	1.18g/cc	ASTM D792
Maximum Moisture Content	0.010	0.010	Injection Molding
Linear Mold Shrinkage, Flow	0.0040-0.0070cm/cm @Thickness 3.20 mm	0.0040-0.0070in/in @Thickness 0.126 in	ASTM D955
Melt Flow	53g/10 min @Load 10.0 kg, Temperature 220 °C	53g/10 min @Load 22.0 lb, Temperature 428 °F	ASTM D1238
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	104	104	ASTM D785
Tensile Strength, Yield	42.2MPa @Thickness 3.20 mm	6120psi @Thickness 0.126 in	50 mm/min; ASTM D638
Elongation at Break	20 % @Thickness 3.20 mm	20 % @Thickness 0.126 in	50 mm/min; ASTM D638
Elongation at Yield	= 5.0 % @Thickness 3.20 mm	= 5.0 % @Thickness 0.126 in	50 mm/min; ASTM D638
Tensile Modulus	2.16GPa @Thickness 3.20 mm	313ksi @Thickness 0.126 in	1 mm/min; ASTM D638
Flexural Yield Strength	69.6MPa @Thickness 6.40 mm	10100psi @Thickness 0.252 in	15 mm/min; ASTM D790
Flexural Modulus	2.55GPa @Thickness 6.40 mm	370ksi @Thickness 0.252 in	15 mm/min; ASTM D790

LG ABS AF312B

特性：

ABS同PS一样是一种加工性能优良的热塑性塑料，可用通用的加工方法加工。 ABS的熔体流动性比PVC和PC好，但比PE、PA及PS差，与POM和HIPS类似；ABS的流动特性属非牛顿流体，其熔体粘度对加工温度和剪切速率都有关系，但对剪切速率更为敏感。

ABS的热稳定性好，不易出现降解现象。ABS的吸水性较高，加工前应进行干燥处理。一般制品的干燥条件为温度80~85℃，时间2~4h；对特殊要求的制品（如电镀）的干燥条件为温度70~80℃，时间18~18h。 ABS制品在加工中易产生内应力，内应力的大小可通过浸入冰乙酸中检验；如应力太大和制品对应力开裂绝对禁止，应进行退火处理，具体条件为放于70~80℃的热风循环干燥箱内2~4h，再冷却至室温即可。

用途 ：

ABS树脂的最大应用领域是汽车、电子电器和建材。汽车领域的使用包括汽车仪表板、车身外板、内装饰板、方向盘、隔音板、门锁、保险杠、通风管等很多部件。在电器方面则广泛应用于电冰箱、电视机、洗衣机、空调器、计算机、复印机等电子电器中。建材方面，ABS管材、ABS卫生洁具、ABS装饰板广泛应用于建材工业。此外ABS还广泛的应用于包装、家具、体育和娱乐用品、机械和仪表工业中。 ABS树脂广泛应用于汽车工业.电器仪表工业和机械工业中,常作齿轮,汽车配件,挡泥板,扶手,冰箱内衬,叶片,轴承,把手,管道,接头,仪表壳,仪表板,盆安全帽等:在家用电器和家用电子设备的应用前景更广阔,如电视机,收录机,冰箱,冷柜,洗衣机,空调机,吸尘器和各种小家电器材:日用品有鞋,包,各种旅游箱,办公设备,玩具及各种容器等,低发泡的ABS能代替木材,适合作建材,家具和家庭用品