Physical Properties物理性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Density密度
|
0.900-0.910g/cc
|
0.0325-0.0329lb/in3
|
base resin; ISO 1183
|
|
Melt Flow熔体流动速率
|
8.0g/10 min @Load 2.16 kg, Temperature 230 °C |
8.0g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133
|
|
Mechanical Properties力学性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Film Elongation at Break,断裂伸长率MD
|
500 - 700 %
|
500 - 700 %
|
ISO 527-3
|
|
Film Elongation at Break,断裂伸长率TD
|
500 - 700 %
|
500 - 700 %
|
ISO 527-3
|
|
Tensile Modulus拉伸模量
|
0.650-0.750GPa
|
94.3-109ksi
|
MD/TD; ISO 527-3
|
|
Flexural Modulus弯曲弹性模量
|
1.45GPa
|
210ksi
|
ISO 178
|
|
Dart Drop, Total Energy落锤冲击测试总能量
|
8.85ft-lb @Thickness 0.00197 in |
1100N; ISO 7765-2
|
|
|
Coefficient of Friction摩擦系数
|
= 0.70
|
= 0.70
|
film to film; ISO 8295
|
|
Film Tensile Strength at Break,薄膜断裂时的拉伸强度MD
|
30.0-50.0MPa
|
4350-7250psi
|
ISO 527-3
|
|
Film Tensile Strength at Break,薄膜断裂时的拉伸强度TD
|
25.0-45.0MPa
|
3630-6530psi
|
ISO 527-3
|
|
Thermal Properties热性能
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Melting Point熔点
|
162-166°C
|
324-331°F
|
DSC; ISO 3146
|
|
Vicat Softening Point维卡软化点
|
154°C @Load 1.02 kg |
309°F @Load 2.25 lb |
A50; ISO 306
|
|
Optical Properties光学性质
|
Metric公制数据
|
English英制数据
|
Comments测试方法
|
|
Haze雾度
|
= 2.0 %
|
= 2.0 %
|
ASTM D1003
|
Gloss光泽度 |
= 120 %
|
= 120 %
|
20° of arc; ASTM D2457
|