MVR(300°C/1.2 kg)9.0 cm3/10 min;阻燃剂;UL 94V-0/1.5 mm和5VA/3.0 mm;中等粘度;易释放;注射成型-熔融温度280-320°C;仅提供不透明颜色 MVR (300 °C/1.2 kg) 9.0 cm3/10 min; flame retardant; UL 94V-0/1.5 mm and 5VA/3.0 mm; medium viscosity; easy release; injection molding - melt temperature 280 - 320 °C; available in opaque colors only |
产品描述Product Description
厂家:德国科思创Covestro - PUR
类别:PCPolycarbonate
颜色:不透明,可用颜色
加工条件:注射成型Injection Molding
性能特点:防火阻燃等级V-1; 防火阻燃等级V-0; 含脱模剂; 阻燃; 防火阻燃等级5VA;Good stripping performance,Flame Characteristics,V-1,V-0,5VA
技术参数Technical Data | |||
---|---|---|---|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
密度 | 1.20 | g/cm3 | ISO 1183 |
表观密度 | 0.64 | g/cm3 | ISO 60 |
熔体质量流动速率 | |||
300℃,1.20kg | 10 | g/10min | ISO 1133 |
熔体体积流动速率 | |||
300℃,1.2 kg | 9.00 | cm3/10min | ISO 1133 |
收缩率 | |||
TD | 0.60 to 0.80 | % | ISO 2577 |
MD | 0.60 to 0.80 | % | ISO 2577 |
TD:2.0 mm | 0.70 | % | ISO 294-4 |
MD:2.0 mm | 0.65 | % | ISO 294-4 |
吸水率 | |||
饱和,23℃ | 0.30 | % | ISO 62 |
平衡,23℃,50% RH | 0.12 | % | ISO 62 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
简支梁缺口冲击强度 | ISO 7391 | ||
-30℃,完全断裂 | 14 | kJ/m2 | ISO 7391 |
23℃,局部断裂 | 70 | kJ/m2 | ISO 7391 |
简支梁无缺口冲击强度 | ISO 179/1eU | ||
-60℃ | No Break | ISO 179/1eU | |
-30℃ | No Break | ISO 179/1eU | |
23℃ | No Break | ISO 179/1eU | |
悬臂梁缺口冲击强度 | ISO 7391 | ||
-30℃,完全断裂 | 12 | kJ/m2 | ISO 7391 |
23℃,局部断裂 | 65 | kJ/m2 | ISO 7391 |
多轴向仪器化冲击能量 | ISO 6603-2 | ||
-30℃ | 55.0 | J | ISO 6603-2 |
23℃ | 50.0 | J | ISO 6603-2 |
多轴向仪器化冲击力峰值 | ISO 6603-2 | ||
-30℃ | 6000 | N | ISO 6603-2 |
23℃ | 5200 | N | ISO 6603-2 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
热变形温度 | |||
1.8 MPa,未退火 | 124 | ℃ | ISO 75-2/A |
0.45 MPa,未退火 | 136 | ℃ | ISO 75-2/B |
玻璃化转变温度 | 142 | ℃ | ISO 11357-2 |
维卡软化温度 | |||
B50 | 144 | ℃ | ISO 306 |
B120 | 145 | ℃ | ISO 306/B120 |
球压测试 | |||
136℃ | Pass | IEC 60695-10-2 | |
线性热膨胀系数 | |||
TD:23~55℃ | 6.5E-5 | 1/℃ | ISO 11359-2 |
MD:23~55℃ | 6.5E-5 | 1/℃ | ISO 11359-2 |
导热系数 | |||
23℃ | 0.20 | W/m/K | ISO 8302 |
相对温度指数 | |||
电气性能,1.50 mm | 125 | ℃ | UL 746 |
强度机械性能,1.50 mm | 125 | ℃ | UL 746 |
冲击机械性能,1.50 mm | 115 | ℃ | UL 746 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
表面电阻率 | 1.0E+16 | ohms | IEC 60093 |
体积电阻率 | |||
23℃ | 1.0E+16 | ohms·cm | IEC 60093 |
介电强度 | |||
23 ℃,1 mm | 34 | kV/mm | IEC 60243-1 |
相对电容率 | IEC 60250 | ||
23℃,100 Hz | 3.10 | IEC 60250 | |
23℃,1 MHz | 3.00 | IEC 60250 | |
耗散因数 | IEC 60250 | ||
23℃,100 Hz | 8.0E-4 | IEC 60250 | |
23℃,1 MHz | 9.0E-3 | IEC 60250 | |
相比漏电起痕指数 | IEC 60112 | ||
解决方案 A | 225 | V | IEC 60112 |
解决方案 B | 125 | V | IEC 60112 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
阻燃等级 | UL 94 | ||
0.75 mm | V-1 | UL 94 | |
1.50 mm | V-0 | UL 94 | |
3.00 mm | 5VA | UL 94 | |
灼热丝可燃性指数 | IEC 60695-2-12 | ||
0.75 mm | 960 | ℃ | IEC 60695-2-12 |
1.5 mm | 960 | ℃ | IEC 60695-2-12 |
3.0 mm | 960 | ℃ | IEC 60695-2-12 |
灼热丝起燃温度 | IEC 60695-2-13 | ||
0.75 mm | 875 | ℃ | IEC 60695-2-13 |
1.5 mm | 875 | ℃ | IEC 60695-2-13 |
3 mm | 875 | ℃ | IEC 60695-2-13 |
极限氧指数 | 36 | % | ISO 4589-2 |
小型燃烧器火焰的应用 | |||
Method K and F,2.00 mm | K1, F1 | DIN 53438-1, -3 | |
燃烧速率 | |||
USFMVSS, 1.00 mm | passed | ISO 3795 | |
Flash Ignition Temperature | 460 | ℃ | ASTM D1929 |
Glow Wire Test | EDF HN60 E.02 | ||
1.50 mm | 750 | ℃ | EDF HN60 E.02 |
3.00 mm | 750 | ℃ | EDF HN60 E.02 |
针焰测试 | IEC 60695-11-5 | ||
Method F:1.50 mm | 2.0 | min | IEC 60695-11-5 |
Method F:2.00 mm | 2.0 | min | IEC 60695-11-5 |
Method F:3.00 mm | 2.0 | min | IEC 60695-11-5 |
Method K:1.50 mm | 2.0 | min | IEC 60695-11-5 |
Method K:2.00 mm | 2.0 | min | IEC 60695-11-5 |
Method K:3.00 mm | 2.0 | min | IEC 60695-11-5 |
自燃温度 | 540 | ℃ | ASTM D1929 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
电解腐蚀 | |||
23℃ | A1 | IEC 60426 | |
ISO Shortname | ISO 7391-PC,MFR,(,,)-09-9 | ||
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
拉伸模量 | |||
23℃ | 2400 | MPa | ISO 527-1-2 |
拉伸强度 | |||
断裂,23℃ | 65.0 | MPa | ISO 527-2/50 |
屈服,23℃ | 66.0 | MPa | ISO 527-2/50 |
拉伸应变 | |||
断裂,23℃ | 120 | % | ISO 527-2/50 |
屈服,23℃ | 6.1 | % | ISO 527-2/50 |
标称拉伸断裂应变 | |||
23℃ | 50 | % | ISO 527-2/50 |
Tensile Creep Modulus(1 hr) | 2200 | MPa | ISO 899-1 |
拉伸蠕变模量 | |||
1000 hr | 1900 | MPa | ISO 899-1 |
弯曲模量 | |||
23℃ | 2400 | MPa | ISO 178 |
弯曲强度 | ISO 178 | ||
3.50% 应变,23℃ | 74.0 | MPa | ISO 178 |
23℃ | 98.0 | MPa | ISO 178 |
弯曲应变 | 7.1 | % | ISO 178 |
球压硬度 | 115 | MPa | ISO 2039-1 |