| Leona? 93G33是一种聚酰胺66（尼龙66）产品,含有的填充物为33% 玻璃纤维增强材料。 它,在亚太地区、北美洲、欧洲或非洲和中东有供货。 Leona? 93G33的应用领域包括工业应用、工程/工业配件、汽车行业 和 纺织/纤维。 特性包括: 阻燃/额定火焰 美观 高刚度 高强度 高流动性 Leona? 93G33 is a Polyamide 66 (Nylon 66) product filled with 33% glass fiber. It is available in Africa Middle East, Asia Pacific, Europe, or North America. Applications of Leona? 93G33 include automotive, engineering/industrial parts, fabrics/fibers and industrial applications. Characteristics include: Flame Rated Good Aesthetics High Flow High Stiffness High Strength |
产品描述Product Description
厂家：日本旭化成Asahi Kasei Corporation
类别：PA66PA66
用途：织物;汽车领域的应用;工业应用;构件;
性能特点：防火阻燃等级HB; 机械强度好; 流动性高; 表面光泽度好;Good Rigidity,Good surface appearance,High liquidity,HB
填料：玻璃纤维 33
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.39 | g/cm3 | ASTM D792 |
| 密度Density | 1.39 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | Internal Method | ||
| TDAcross Flow | 0.80 | % | 内部方法 |
| MDFlow | 0.30 | % | 内部方法 |
| 吸水率吸水率 | |||
| 饱和，23℃饱和，23℃ | -- | % | |
| 平衡，23℃，50% RH平衡，23℃，50% RH | -- | % | ISO 62 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | 12 | kJ/m2 | ISO 179 |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | 98 | kJ/m2 | ISO 179 |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | 130 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 210 | ℃ | ISO 75-2/A |
| 1.8 MPa，未退火1.8 MPa，未退火 | 210 | ℃ | ASTM D648 |
| 0.45 MPa，未退火0.45 MPa，未退火 | 230 | ℃ | ISO 75-2/B |
| 线性热膨胀系数线性热膨胀系数 | |||
| MDMD | 3.0E-5 | 1/℃ | ASTM D696 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级0.75 mm | |||
| 0.75 mm | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量拉伸模量 | |||
| 23℃23℃ | 9400 | MPa | ISO 527-2 |
| 拉伸强度Tensile Strength | 167 | MPa | ASTM D638 |
| 断裂，23℃断裂，23℃ | 174 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 断裂，23℃断裂，23℃ | 5.5 | % | ISO 527-2 |
| 断裂断裂 | 4.0 | % | ASTM D638 |
| 弯曲模量Flexural Modulus | 8600 | MPa | ASTM D790 |
| 23℃23℃ | 7300 | MPa | ISO 178 |
| 弯曲强度Flexural Strength | 275 | MPa | ASTM D790 |
| 23℃23℃ | 233 | MPa | ISO 178 |
| 洛氏硬度洛氏硬度 | |||
| M 级M 级 | 90 | ISO 2039-2 | |
| M 级M 级 | 90 | ASTM D785 | |