| Ultramid? A3WG10是一种50%玻璃纤维增强耐热注塑成型PA66级。典型应用包括具有极高刚性的工业制品。 Ultramid A3WG10 is a 50% glass fiber reinforced and heat aging resistance injection molding PA66 grade. Applications Typical applications include industrial articles having very high rigidity. |
产品描述Product Description
厂家：德国巴斯夫BASF Polyurethanes GmbH
类别：PA66PA66
用途：工业应用;
加工条件：注射成型Injection Molding
性能特点：机械强度好; 耐老化;Good Rigidity,Good heat aging resistance
填料：玻璃纤维 50
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.55 | g/cm3 | ISO 1183 |
| 吸水率Water Absorption | |||
| 23℃，24hr(23°C, 24 hr) | 4.00 | % | ISO 62 |
| 23℃，50% RH(23°C, 50RH) | 1.20 | % | ISO 62 |
| 熔体质量流动速率熔融流动指数 | |||
| 275℃，5.0kg275℃ / 5.0Kg | 20.00 | g/10min | ISO 1133 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度 | |||
| 23℃23°C | 230 | MPa | ISO 527-2 |
| 拉伸应变Tensile Elongation at Break | |||
| 断裂，23℃23°C | 2.5 | % | ISO 527-2 |
| 拉伸模量Tensile Modulus | |||
| 23℃23°C | 16800 | MPa | ISO 527-2 |
| 弯曲模量Flexural Modulus | |||
| 23℃23°C | 15000 | MPa | ISO 178 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Heat Deflection Temperature | |||
| 0.45 MPa，未退火0.45MPa 未退火 | 250 | ℃ | ISO 75-2/Bf |
| 1.8 MPa，退火1.80MPa 退火 | 250 | ℃ | ISO 75-2/Af |
| 熔融温度Melting Temperature | 260 | ℃ | ISO 11357-3 |
| 维卡软化温度Vicat Softening Temperature | |||
| 线性热膨胀系数线膨胀系数 | |||
| MDMD | 1.3E-5 | 1/℃ | ISO 11359-2 |
| TDTD | 5.5E-5 | 1/℃ | ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻体积电阻 | 1.0E+10 | Ω.cm | IEC 60093 |
| 绝缘强度绝缘强度 | |||
| 12 | KV/mm | IEC 60243-1 | |
| 介电常数Dielectric Constant | |||
| 23℃23°C | 3.80 | 1 MHz | IEC 60250 |
| 耗散因数Dissipation Factor | |||
| 23℃ 23°C | 0.015 | 100 Hz | IEC 60250 |
| 23℃ 23°C | 0.015 | 1 MHz | IEC 60250 |
| 相比漏电起痕指数相对漏电起痕指数 | 450 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级防火等级 | |||
| 0.75mm | HB | UL-94 | |
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | |||
| 23℃23°C | 95 | kJ/m2 | ISO 179/1eU |
| -30℃-30°C | 85 | kJ/m2 | ISO 179/1eU |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | |||
| 23℃23°C | 18 | kJ/m2 | ISO 179/1eA |
| -30℃-30°C | 13 | kJ/m2 | ISO 179/1eA |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃23°C | 130 | kJ/m2 | ISO 180-1A |
| -40℃-40°C | 100 | kJ/m2 | ISO 180-1A |