江苏普及塑料有限公司
| 牌号简介About |
|---|
| Ultramid? C3U是一种注射成型，通用PA6/66级，具有改进的阻燃性。该产品的最小厚度为0.4 mm，经UL认证为94V0。用途：用于抗冲击电气绝缘部件，如接触座和插头连接条。 Ultramid C3U is an injection molding, general purpose PA6/66 grade with improved flame retardance. The product is UL recognized as 94V0 at 0.4 mm minimum thickness. Applications It is used for impact resistant electrical insulating parts such as contact bases and plug connector strips. |
产品描述Product Description
厂家：德国巴斯夫BASF Polyurethanes GmbH
类别：PA66/6PA66/6
用途：电气元件;通用;电子绝缘;
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级V-0; 阻燃; 冲击性能好;High impact resistance,Flame Characteristics,V-0
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.16 | g/cm3 | ASTM D792 |
| 密度Density | 1.16 | g/cm3 | ISO 1183 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 275℃，5 kg275℃/5.0 kg | 140 | cm3/10min | ISO 1133 |
| 收缩率收缩率 | |||
| MD：3.2 mmMD，3.18 mm | 0.80 | % | |
| 吸水率吸水率 | |||
| 饱和，23℃饱和，23℃ | 8.5 | % | ISO 62 |
| 饱和饱和 | 8.5 | % | ASTM D570 |
| 平衡，23℃，50% RH平衡，23℃，50% RH | 2.9 | % | ISO 62 |
| 平衡，50% RHEquilibrium，50% RH | 2.9 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179 | ||
| -30℃-30°C | 4.0 | kJ/m2 | ISO 179 |
| 23℃23°C | 9.0 | kJ/m2 | ISO 179 |
| 简支梁无缺口冲击强度简支梁无缺口冲击强度 | |||
| 23℃23℃ | 80 | kJ/m2 | ISO 179 |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | ASTM D256 | ||
| 23℃23℃ | 4.5 | kJ/m2 | ISO 180 |
| -40℃-40°C | 32 | J/m | ASTM D256 |
| 23℃23°C | 43 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 70.0 | ℃ | ISO 75-2/A |
| 1.8 MPa，未退火1.8 MPa，未退火 | 91.0 | ℃ | ASTM D648 |
| 0.45 MPa，未退火0.45 MPa，未退火 | 224 | ℃ | ASTM D648 |
| 熔融峰值温度Peak Melting Temperature | 243 | ℃ | ASTM D3418 |
| 熔融温度溶融温度 | |||
| DSCDSC | 243 | ℃ | ISO 3146 |
| 线性热膨胀系数线性热膨胀系数 | |||
| TDTD | 9.0E-5 | 1/℃ | |
| MDMD | 4.0E-5 | 1/℃ | ASTM E831 |
| MDMD | 8.0E-5 | 1/℃ | |
| 相对温度指数相对温度指数 | |||
| 电气性能电气性能 | UL 746 | ||
| 阻燃等级（0.38 mm）0.38 mm | 110 | ℃ | UL 746 |
| 0.75 mm0.75 mm | 120 | ℃ | UL 746 |
| 3.0 mm3.0 mm | 120 | ℃ | UL 746 |
| 强度机械性能强度机械性能 | UL 746 | ||
| 0.75 mm0.75 mm | 115 | ℃ | UL 746 |
| 1.5 mm1.5 mm | 120 | ℃ | UL 746 |
| 冲击机械性能冲击机械性能 | UL 746 | ||
| 阻燃等级（0.38 mm）0.38 mm | 65.0 | ℃ | UL 746 |
| 0.75 mm0.75 mm | 105 | ℃ | UL 746 |
| 1.5 mm1.5 mm | 105 | ℃ | UL 746 |
| 3.0 mm3.0 mm | 105 | ℃ | UL 746 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻率Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| 1.50 mm1.50 mm | 1.0E+13 | ohms·cm | ASTM D257 |
| 介电强度Electric Strength | 32 | kV/mm | IEC 60243-1 |
| 介电常数介电常数 | |||
| 1 MHz1 MHz | 3.60 | IEC 60250 | |
| 耗散因数耗散因数 | |||
| 1 MHz1 MHz | 0.020 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | 600 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.38 mm0.38 mm | V-0 | UL 94 | |
| 0.75 mm0.75 mm | V-0 | UL 94 | |
| 1.50 mm1.5 mm | V-0 | UL 94 | |
| 3.00 mm3.0 mm | V-0 | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量拉伸模量 | |||
| 23℃23℃ | 3500 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |||
| 屈服，23℃屈服，23℃ | 83.0 | MPa | ASTM D638 |
| 屈服，23℃屈服，23℃ | 75.0 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 断裂，23℃断裂，23℃ | 50 | % | ASTM D638 |
| 屈服，23℃屈服，23℃ | 5.0 | % | ASTM D638 |
| 屈服，23℃屈服，23℃ | 4.0 | % | ISO 527-2 |
| 标称拉伸断裂应变标称拉伸断裂应变 | |||
| 23℃23℃ | 6.0 | % | ISO 527-2 |
| 弯曲模量弯曲模量 | |||
| 23℃23℃ | 3000 | MPa | ASTM D790 |
| 23℃23℃ | 3000 | MPa | ISO 178 |
| 球压硬度Ball Indentation Hardness | 100 | MPa | ISO 2039- |