江苏普及塑料有限公司
| 牌号简介About |
|---|
| Ultramid? A3WG6是一种30%玻璃纤维增强和耐热注塑成型PA66等级机械部件和外壳的高刚度和尺寸稳定性。典型应用包括灯插座外壳、冷却风扇、铝窗框的绝缘型材、汽车冷却系统的水容器。 Ultramid A3WG6 is a 30% glass fiber reinforced and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. Applications Typical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems. |
产品描述Product Description
厂家：德国巴斯夫BASF Polyurethanes GmbH
类别：PA66PA66
用途：汽车领域的应用;机器/机械部件;容器;绝缘材料;外壳;
加工条件：注射成型Injection Molding
性能特点：耐热性好; 机械强度好; 耐油; 尺寸稳定性好;Good Rigidity,Good Dimensional Stability,Grease resistance,Heat Resistance, Good
填料：玻璃纤维 30
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.36 | g/cm3 | ISO 1183 |
| 吸水率Water Absorption | |||
| 23℃，24hr(23°C, 24 hr) | 5.5 | % | ISO 62 |
| 23℃，50% RH(23°C, 50RH) | 1.7 | % | ISO 62 |
| 熔体质量流动速率熔融流动指数 | |||
| 275℃，5.0kg275℃ / 5.0Kg | 40 | g/10min | ISO 1133 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度 | |||
| 23℃23°C | 190 | MPa | ISO 527-2 |
| 拉伸应变Tensile Elongation at Break | |||
| 断裂，23℃23°C | 3.0 | % | ISO 527-2 |
| 拉伸模量Tensile Modulus | |||
| 23℃23°C | 10000 | MPa | ISO 527-2 |
| 弯曲模量Flexural Modulus | |||
| 23℃23°C | 8600 | MPa | ISO 178 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Heat Deflection Temperature | |||
| 0.45 MPa，未退火0.45MPa 未退火 | 250 | ℃ | ISO 75-2/Bf |
| 1.8 MPa，退火1.80MPa 退火 | 250 | ℃ | ISO 75-2/Af |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻体积电阻 | 1.0E+13 | Ω.cm | IEC 60093 |
| 介电常数Dielectric Constant | |||
| 23℃23°C | 3.5 | 1 MHz | IEC 60250 |
| 耗散因数Dissipation Factor | |||
| 23℃ 23°C | 0.014 | 100 Hz | IEC 60250 |
| 23℃ 23°C | 0.014 | 1 MHz | IEC 60250 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级防火等级 | |||
| 0.71mm | HB | UL-94 | |
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | |||
| 23℃23°C | 85 | kJ/m2 | ISO 179/1eU |
| -30℃-30°C | 70 | kJ/m2 | ISO 179/1eU |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | |||
| 23℃23°C | 13 | kJ/m2 | ISO 179/1eA |
| -30℃-30°C | 11 | kJ/m2 | ISO 179/1eA |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃23°C | 12 | kJ/m2 | ISO 180-1A |