江苏普及塑料有限公司
| 牌号简介About |
|---|
| Ultramid? A3EG3是一种15%玻璃纤维增强注塑成型PA66级。典型应用包括中等硬度的机械部件和外壳，以及电绝缘部件。 Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. Applications Typical applications include medium stiffness machinery components and housings, as well as electrically insulating parts. |
产品描述Product Description
厂家：德国巴斯夫BASF Polyurethanes GmbH
类别：PA66PA66
用途：电气元件;机器/机械部件;外壳;电子绝缘;
加工条件：注射成型Injection Molding
性能特点：机械强度好; 耐油;Good Rigidity,Grease resistance
填料：玻璃纤维 15
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.23 | g/cm3 | ISO 1183 |
| 吸水率Water Absorption | |||
| 23℃，24hr(23°C, 24 hr) | 6.70-7.30 | % | ISO 62 |
| 熔体质量流动速率熔融流动指数 | |||
| ℃ / Kg | 70 | g/10min | ISO 1133 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸强度拉伸强度 | |||
| 23℃23°C | 130 | MPa | ISO 527-2 |
| 拉伸应变Tensile Elongation at Break | |||
| 断裂，23℃23°C | 3 | % | ISO 527-2 |
| 拉伸模量Tensile Modulus | |||
| 23℃23°C | 6000 | MPa | ISO 527-2 |
| 拉伸蠕变模量Tensile Creep Modulus | |||
| 1000 Hr1000 Hr | MPa | ISO 899-1 | |
| 弯曲强度Flexural Strength | |||
| 23℃23°C | 180 | MPa | ISO 178 |
| 弯曲模量Flexural Modulus | |||
| 23℃23°C | 5500 | MPa | ISO 178 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Heat Deflection Temperature | |||
| 0.45 MPa，未退火0.45MPa 未退火 | 250 | ℃ | ISO 75-2/Bf |
| 1.8 MPa，退火1.80MPa 退火 | 250 | ℃ | ISO 75-2/Af |
| 导热系数Thermal Conductivity | 0.33 | W/m/K | DIN 52612 |
| 线性热膨胀系数线膨胀系数 | |||
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 体积电阻体积电阻 | 1.0E+12 | Ω.cm | IEC 60093 |
| 绝缘强度绝缘强度 | |||
| 21 | KV/mm | IEC 60243-1 | |
| 介电常数Dielectric Constant | |||
| 23℃23°C | 3.50 | 1 kHz | IEC 60250 |
| 耗散因数Dissipation Factor | |||
| 23℃ 23°C | 140E-4 | 1 MHz | IEC 60250 |
| 相比漏电起痕指数相对漏电起痕指数 | 550 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级防火等级 | |||
| 0.80mm | HB | UL-94 | |
| 1.70mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | |||
| 23℃23°C | 45 | kJ/m2 | ISO 179/1eU |
| -30℃-30°C | 43 | kJ/m2 | ISO 179/1eU |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | |||
| 23℃23°C | 8 | kJ/m2 | ISO 179/1eA |
| -30℃-30°C | 7 | kJ/m2 | ISO 179/1eA |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃23°C | 5.5 | kJ/m2 | ISO 180-1A |