RN001S
| 牌号简介About |
|---|
| LNP Lubricomp RN001S化合物LNP Lubricomp RN001S是基于含有2%MoS2的尼龙66树脂的化合物。这种材料的附加特性包括：耐磨、热稳定。也被称为：lnp*lubricomp*化合物nykon r-hs产品再订购名称：rn001s lnp lubricomp rn001s化合物lnp lubricomp rn001s是基于含有mos2的尼龙66树脂的化合物。这种材料的附加特性包括：内部润滑，热稳定。又称：LNP*Lubricomp*化合物R-HS产品再订购名称：RN001SLNP Lubricomp RN001S化合物润滑聚酰胺66注塑树脂。也称为：lnp*lubricomp*化合物rl4210s1产品再订购名称：rn001s LNP LUBRICOMP RN001S is a compound based on Nylon 66 resin containing 2% MOS2. Added features of this material include: Wear Resistant, Heat Stabilized. |
产品描述Product Description
厂家：沙特沙伯基础SABIC
类别：PA66PA66
加工条件：注射成型Injection Molding
性能特点：热稳定性好; 耐磨; 润滑性;Lubricating,Good wear resistance,Heat Stabilized
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.16 | g/cm3 | ASTM D792 |
| 密度Density | 1.17 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | ISO 294-4 | ||
| TD：24 hrsAcross Flow : 24 hr | 1.0 | % | ISO 294-4 |
| MD：24 hrsFlow : 24 hr | 1.0 | % | ISO 294-4 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus 22 | 4140 | MPa | ASTM D638 |
| 拉伸模量Tensile Modulus | 3910 | MPa | ISO 527-1-2 |
| 拉伸强度拉伸强度 | |||
| 断裂断裂 | 69.0 | MPa | ISO 527-2 |
| 断裂断裂 | 84.1 | MPa | ASTM D638 |
| 屈服屈服 | 84.1 | MPa | ASTM D638 |
| 屈服屈服 | 69.0 | MPa | ISO 527-2 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 42 | % | ISO 527-2 |
| 断裂断裂 | 3.8 | % | ASTM D638 |
| 屈服屈服 | 2.1 | % | ISO 527-2 |
| 屈服屈服 | 2.9 | % | ASTM D638 |
| 弯曲模量Flexural Modulus | 3450 | MPa | ASTM D790 |
| 弯曲模量Flexural Modulus | 3400 | MPa | ISO 178 |
| 弯曲强度Flexural Stress | 107 | MPa | ISO 178 |
| 摩擦系数Coefficient of Friction | ASTM D3702 Modified | ||
| 动态Dynamic | 0.75 | ASTM D3702 Modified | |
| 静态Static | 0.55 | ASTM D3702 Modified | |
| 磨损因数磨损因数 | |||
| WasherWasher | 103 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度 | |||
| 23℃23℃3 | 2.8 | kJ/m2 | ISO 180-1A |
| 23℃23℃ | 27 | J/m | ASTM D256 |
| 23℃23℃ | 1100 | J/m | ASTM D4812 |
| 悬臂梁无缺口冲击强度悬壁梁无缺口冲击强度3 | |||
| 23℃23℃3 | 54 | kJ/m2 | ISO 180/1U |
| 装有测量仪表的落镖冲击装有测量仪表的落镖冲击 | |||
| 23℃，Energy at Peak Load23℃，Energy at Peak Load | 2.30 | J | ASTM D3763 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火，64 mm跨距1.8 MPa，未退火，64.0 mm 跨距4 | 301 | ℃ | ISO 75-2/Af |
| 1.8 MPa，未退火，3.2 mm1.8 MPa，未退火，3.20 mm | 76.7 | ℃ | ASTM D648 |
| 0.45 MPa，未退火，64 mm跨距0.45 MPa，未退火，64.0 mm Span4 | 223 | ℃ | ISO 75-2/Bf |
| 0.45 MPa，未退火，3.2 mm0.45 MPa，未退火，3.20 mm | 231 | ℃ | ASTM D648 |