江苏普及塑料有限公司
RL-4540
| 牌号简介About |
|---|
| LNP Lubricomp RP004S是一种基于尼龙66的化合物，含有聚四氟乙烯/硅酮。这一等级的附加功能包括：热稳定，耐磨。也称为：LNP*Lubricomp*化合物RL-4540 HS产品再订购名称：RP004S |
产品描述Product Description
厂家：沙特沙伯基础SABIC
类别：PA66PA66
加工条件：注射成型Injection Molding
性能特点：热稳定性好; 耐磨; 润滑性;Lubricating,Good wear resistance,Heat Stabilized
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.24 | g/cm3 | ASTM D792 |
| 密度Density | 1.24 | g/cm3 | ISO 1183 |
| 收缩率收缩率 | |||
| TD：24 hrsTD，24 hr | 1.0 to 3.0 | % | ASTM D955 |
| MD：24 hrsMD，24小时 | 1.0 to 3.0 | % | ASTM D955 |
| 吸水率吸水率 | |||
| 平衡，23℃，50% RH平衡，23℃，50% RH | 1.2 | % | ISO 62 |
| 24hr，50% RH24 hr，50% RH | 0.86 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus 22 | 2950 | MPa | ASTM D638 |
| 拉伸模量Tensile Modulus | 2760 | MPa | ISO 527-1-2 |
| 拉伸强度拉伸强度3 | |||
| 断裂断裂 | 64.0 | MPa | ISO 527-2/5 |
| 断裂断裂3 | 59.0 | MPa | ASTM D638 |
| 屈服屈服 | 65.0 | MPa | ISO 527-2/5 |
| 屈服屈服3 | 61.0 | MPa | ASTM D638 |
| 拉伸应变拉伸应变 | |||
| 断裂断裂 | 19 | % | ISO 527-2/5 |
| 断裂断裂4 | 18 | % | ASTM D638 |
| 屈服屈服3 | 4.8 | % | ASTM D638 |
| 屈服屈服 | 4.8 | % | ISO 527-2/5 |
| 弯曲模量Flexural Modulus 55 | 2230 | MPa | ISO 178 |
| 50 mm跨距50.0 mm 跨距4 | 2150 | MPa | ASTM D790 |
| 弯曲强度Flexural Stress | 78.0 | MPa | ISO 178 |
| 摩擦系数Coefficient of Friction | ASTM D3702 Modified | ||
| 动态Dynamic | 0.23 | ASTM D3702 Modified | |
| 静态Static | 0.11 | ASTM D3702 Modified | |
| 磨损因数Wear Factor | ASTM D3702 Modified | ||
| RingRing | -0.200 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| WasherWasher | 4.50 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度悬壁梁缺口冲击强度 | |||
| 23℃23℃ | 46 | J/m | ASTM D256 |
| 23℃23℃6 | 5.4 | kJ/m2 | ISO 180-1A |
| 23℃23℃ | 1400 | J/m | ASTM D4812 |
| 悬臂梁无缺口冲击强度悬臂梁无缺口冲击强度5 | |||
| 23℃23℃5 | 120 | kJ/m2 | ISO 180/1U |
| 装有测量仪表的落镖冲击装有测量仪表的落镖冲击 | |||
| 23℃，Total Energy23℃，Total Energy | 3.80 | J | ASTM D3763 |
| 多轴向仪器化冲击能量Multi-Axial Instrumented Impact Energy | 2.80 | J | ISO 6603-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火，64 mm跨距1.8 MPa，未退火，64.0 mm 跨距7 | 57.0 | ℃ | ISO 75-2/Af |
| 1.8 MPa，未退火，3.2 mm1.8 MPa，未退火，3.20 mm | 57.0 | ℃ | ASTM D648 |
| 0.45 MPa，未退火，64 mm跨距0.45 MPa，未退火，64.0 mm Span7 | 154 | ℃ | ISO 75-2/Bf |
| 0.45 MPa，未退火，3.2 mm0.45 MPa，未退火，3.20 mm | 184 | ℃ | ASTM D648 |