| 牌号简介About |
|---|
| LNP Lubricomp RFL36XXY是一种基于尼龙66的化合物，含有30%的玻璃纤维和15%的聚四氟乙烯。这一等级的附加特征是：耐磨。又名：lnp*lubricomp*化合物RFL-4036产品再订购名称：RFL36XXY |
产品描述Product Description
厂家：沙特沙伯基础SABIC
类别：PA66PA66
加工条件：注射成型Injection Molding
性能特点：耐磨; 润滑性;Lubricating,Good wear resistance
填料：玻璃纤维 30
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.51 | g/cm3 | ASTM D792 |
| 密度Density | 1.51 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | ISO 294-4 | ||
| TD：24 hrsTD，24 hr | 1.1 | % | ASTM D955 |
| MD：24 hrsMD，24小时 | 0.50 | % | ASTM D955 |
| TD：24 hrsAcross Flow : 24 hr | 1.2 | % | ISO 294-4 |
| MD：24 hrsFlow : 24 hr | 0.32 | % | ISO 294-4 |
| 吸水率吸水率 | |||
| 24hr，50% RH24 hr，50% RH | 0.62 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus 22 | 11200 | MPa | ASTM D638 |
| 拉伸模量Tensile Modulus | 9800 | MPa | ISO 527-1-2 |
| 拉伸强度拉伸强度3 | |||
| 断裂断裂 | 138 | MPa | ISO 527-2/5 |
| 断裂断裂3 | 139 | MPa | ASTM D638 |
| 拉伸应变拉伸应变4 | |||
| 断裂断裂 | 2.1 | % | ISO 527-2/5 |
| 断裂断裂4 | 2.1 | % | ASTM D638 |
| 弯曲模量Flexural Modulus 55 | 9700 | MPa | ISO 178 |
| 50 mm跨距50.0 mm 跨距4 | 9740 | MPa | ASTM D790 |
| 弯曲强度Flexural Stress | 211 | MPa | ISO 178 |
| 断裂，50 mm跨度断裂，50.0 mm 跨距5 | 236 | MPa | ASTM D790 |
| 摩擦系数Coefficient of Friction | ASTM D3702 Modified | ||
| 动态Dynamic | 0.59 | ASTM D3702 Modified | |
| 静态Static | 0.46 | ASTM D3702 Modified | |
| 磨损因数磨损因数 | |||
| WasherWasher | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact 66 | ISO 180/1A | ||
| 23℃23℃ | 910 | J/m | ASTM D4812 |
| 23℃23℃ | 110 | J/m | ASTM D256 |
| -40℃-40°C | 7.0 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 10 | kJ/m2 | ISO 180-1A |
| 悬臂梁无缺口冲击强度悬臂梁无缺口冲击强度5 | |||
| 23℃23℃5 | 51 | kJ/m2 | ISO 180/1U |
| 装有测量仪表的落镖冲击装有测量仪表的落镖冲击 | |||
| 23℃，Energy at Peak Load23℃，Energy at Peak Load | 10.0 | J | ASTM D3763 |
| 多轴向仪器化冲击能量Multi-Axial Instrumented Impact Energy | 2.89 | J | ISO 6603-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火，64 mm跨距1.8 MPa，未退火，64.0 mm 跨距7 | 248 | ℃ | ISO 75-2/Af |
| 1.8 MPa，未退火，3.2 mm1.8 MPa，未退火，3.20 mm | 249 | ℃ | ASTM D648 |
| 线性热膨胀系数线性热膨胀系数 | |||
| TD：-40~40℃TD：-40 到 40℃ | 5.5E-5 | 1/℃ | ISO 11359-2 |
| TD：-40~40℃TD：-40 到 40℃ | 5.5E-5 | 1/℃ | ASTM E831 |
| MD：-40~40℃MD：-40 到 40℃ | 3.8E-5 | 1/℃ | ISO 11359-2 |
| MD：-40~40℃MD：-40 到 40℃ | 3.8E-5 | 1/℃ | ASTM E831 |