江苏普及塑料有限公司
| 牌号简介About |
|---|
| 用于食品接触应用的无增强聚酰胺66 Unreinforced Polyamide 66 Developed for Food Contact Applications |
产品描述Product Description
厂家：美国杜邦DuPont Canada, Inc. - Dartek Division
类别：PA66PA66
用途：非特定食品应用;
加工条件：注射成型Injection Molding
性能特点：防火阻燃等级V-2; 食品接触;Food contact compliance,V-2
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸应变拉伸应变 | |||
| 屈服屈服 | 4.5 | % | ISO 527-2 |
| MD，屈服MD，屈服 | 4.5 | % | ISO 527-3 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃-30°C | 4.5 | kJ/m2 | ISO 179/1eA |
| 23℃23°C | 5.5 | kJ/m2 | ISO 179/1eA |
| 简支梁无缺口冲击强度Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30℃-30°C | 400 | kJ/m2 | ISO 179/1eU |
| 23℃23°C | No Break | ISO 179/1eU | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度热变形温度 | |||
| 1.8 MPa，未退火1.8 MPa，未退火 | 70.0 | ℃ | ISO 75-2/A |
| 0.45 MPa，未退火0.45 MPa，未退火 | 190 | ℃ | ISO 75-2/B |
| 玻璃化转变温度Glass Transition Temperature 22 | 60.0 | ℃ | ISO 11357-2 |
| 维卡软化温度维卡软化温度 | |||
| B50B50 | 240 | ℃ | ISO 306 |
| 熔融温度Melting Temperature 22 | 262 | ℃ | ISO 11357-3 |
| 线性热膨胀系数线性热膨胀系数 | |||
| TDTD | 1.1E-4 | 1/℃ | ISO 11359-2 |
| MDMD | 1.0E-4 | 1/℃ | ISO 11359-2 |
| Effective Thermal DiffusivityEffective Thermal Diffusivity | 5.00E-8 | m2/s | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 表面电阻率Surface Resistivity | -- | ohms | IEC 60093 |
| 体积电阻率Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| 介电强度Electric Strength | 32 | kV/mm | IEC 60243-1 |
| 相对电容率Relative Permittivity | IEC 60250 | ||
| 100 Hz100 Hz | 3.80 | IEC 60250 | |
| 1 MHz1 MHz | 3.50 | IEC 60250 | |
| 耗散因数Dissipation Factor | IEC 60250 | ||
| 100 Hz100 Hz | 8.0E-3 | IEC 60250 | |
| 1 MHz1 MHz | 0.018 | IEC 60250 | |
| 相比漏电起痕指数Comparative Tracking Index | 600 | V | IEC 60112 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级Flame Rating | UL 94 | ||
| 0.70 mm0.70 mm | V-2 | UL 94 | |
| 1.50 mm1.5 mm | V-2 | UL 94 | |
| 可燃性等级Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.70 mm0.70 mm | V-2 | IEC 60695-11-10, -20 | |
| 1.5 mm1.5 mm | V-2 | IEC 60695-11-10, -20 | |
| 极限氧指数Oxygen Index | 28 | % | ISO 4589-2 |
| FMVSS 阻燃等级FMVSS Flammability | DNI | FMVSS 302 | |
| 雾化Fogging | ISO 6452 | ||
| F-value（refraction）F-value (refraction) | 99 | % | ISO 6452 |
| G-value（condensate）G-value (condensate) | 1.0E-4 | g | ISO 6452 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 有机化合物的排放Emission of Organic Compounds | 5.00 | μgC/g | VDA 277 |
| OdorOdor | 3.00 | VDA 270 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 拉伸模量Tensile Modulus | 3100 | MPa | ISO 527-2 |
| 拉伸强度拉伸强度 | |||
| 屈服屈服 | 82.0 | MPa | ISO 527-2 |
| 标称拉伸断裂应变Nominal Tensile Strain at Break | 25 | % | ISO 527-2 |
| Tensile Creep Modulus（1 hr）Tensile Creep Modulus (1 hr) | -- | MPa | ISO 899-1 |
| 拉伸蠕变模量拉伸蠕变模量 | |||
| 1000 hr1000 hr | -- | MPa | ISO 899-1 |
| 弯曲模量Flexural Modulus | 2800 | MPa | ISO 178 |
| 洛氏硬度Rockwell Hardness | ISO 2039-2 | ||
| M 级M-Scale | 79 | ISO 2039-2 | |
| R 级R-Scale | 121 | ISO 2039-2 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Density | 1.14 | g/cm3 | ISO 1183 |
| 收缩率Molding Shrinkage | ISO 294-4 | ||
| TDAcross Flow | 1.4 | % | ISO 294-4 |
| MDFlow | 1.4 | % | ISO 294-4 |
| 吸水率吸水率 | |||
| 饱和，23℃，2.00 mmSaturation，23℃，2.00 mm | 8.5 | % | ISO 62 |
| 平衡，23℃，50% RH，2.00 mmEquilibrium，23℃，2.00 mm，50% RH | 2.6 | % | ISO 62 |
| 粘数Viscosity Number | 150 | cm3/g | ISO 307 |
| 熔体密度Melt Density | 0.970 | g/cm3 | |
| 顶出温度Ejection Temperature | 190 | ℃ | |
| Specific Heat Capacity of MeltSpecific Heat Capacity of Melt | 2790 | J/kg/℃ | |
| Thermal Conductivity of MeltThermal Conductivity of Melt | 0.16 | W/m/K | |