33%玻璃纤维增强聚酰胺66 33% Glass Reinforced Polyamide 66 |
产品描述Product Description
厂家:美国杜邦DuPont Canada, Inc. - Dartek Division
类别:PA66PA66
加工条件:注射成型Injection Molding
性能特点:防火阻燃等级HB;HB
填料:玻璃纤维 33
技术参数Technical Data | |||
---|---|---|---|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179/1eA | ||
-40℃-40°C | 10 | kJ/m2 | ISO 179/1eA |
-30℃-30°C | 10 | kJ/m2 | ISO 179/1eA |
23℃23°C | 13 | kJ/m2 | ISO 179/1eA |
简支梁无缺口冲击强度Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-30℃-30°C | 70 | kJ/m2 | ISO 179/1eU |
23℃23°C | 85 | kJ/m2 | ISO 179/1eU |
悬臂梁缺口冲击强度Notched Izod Impact Strength | ISO 180/1A | ||
-40℃-40°C | 10 | kJ/m2 | ISO 180-1A |
-30℃-30°C | 10 | kJ/m2 | ISO 180-1A |
23℃23°C | 12 | kJ/m2 | ISO 180-1A |
悬臂梁无缺口冲击强度Unnotched Izod Impact Strength | ISO 180/1U | ||
-30℃-30°C | 70 | kJ/m2 | ISO 180/1U |
23℃23°C | 80 | kJ/m2 | ISO 180/1U |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
热变形温度热变形温度 | |||
1.8 MPa,未退火1.8 MPa,未退火 | 252 | ℃ | ISO 75-2/A |
0.45 MPa,未退火0.45 MPa,未退火 | 261 | ℃ | ISO 75-2/B |
玻璃化转变温度Glass Transition Temperature 22 | 80.0 | ℃ | ISO 11357-2 |
熔融温度Melting Temperature 22 | 262 | ℃ | ISO 11357-3 |
线性热膨胀系数线性热膨胀系数 | |||
TDTD | ISO 11359-2 | ||
---- | 8.3E-5 | cm/cm/℃ | ISO 11359-2 |
-40 到 23℃-40 to 23°C | 6.5E-5 | cm/cm/℃ | ISO 11359-2 |
55 到 160℃55 to 160°C | 1.4E-4 | cm/cm/℃ | ISO 11359-2 |
MDMD | ISO 11359-2 | ||
---- | 1.8E-5 | cm/cm/℃ | ISO 11359-2 |
-40 到 23℃-40 to 23°C | 2.4E-5 | cm/cm/℃ | ISO 11359-2 |
55 到 160℃55 to 160°C | 1.3E-5 | cm/cm/℃ | ISO 11359-2 |
比热容Specific Heat Capacity 33 | 1330 | J/kg/℃ | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
体积电阻率Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
相对电容率Relative Permittivity | IEC 60250 | ||
100 Hz100 Hz | 4.20 | IEC 60250 | |
1 MHz1 MHz | 4.00 | IEC 60250 | |
耗散因数Dissipation Factor | IEC 60250 | ||
100 Hz100 Hz | 0.010 | IEC 60250 | |
1 MHz1 MHz | 0.015 | IEC 60250 | |
相比漏电起痕指数Comparative Tracking Index | 600 | V | IEC 60112 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
燃烧速率燃烧速率4 | |||
1 mm1.00 mm4 | 28 | mm/min | ISO 3795 |
阻燃等级Flame Rating | UL 94 | ||
0.71 mm0.71 mm | HB | UL 94 | |
1.50 mm1.5 mm | HB | UL 94 | |
可燃性等级Flammability Classification | IEC 60695-11-10, -20 | ||
0.71 mm0.71 mm | HB | IEC 60695-11-10, -20 | |
1.5 mm1.5 mm | HB | IEC 60695-11-10, -20 | |
极限氧指数Oxygen Index | 24 | % | ISO 4589-2 |
FMVSS 阻燃等级FMVSS Flammability | SE/B | FMVSS 302 | |
雾化Fogging | ISO 6452 | ||
F-value(refraction)F-value (refraction) | 95 | % | ISO 6452 |
G-value(condensate)G-value (condensate) | 3.0E-4 | g | ISO 6452 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
有机化合物的排放Emission of Organic Compounds | 6.00 | μgC/g | VDA 277 |
OdorOdor | 4.50 | VDA 270 | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
拉伸模量Tensile Modulus | 10000 | MPa | ISO 527-2 |
拉伸强度拉伸强度 | |||
断裂断裂 | 200 | MPa | ISO 527-2 |
拉伸应变拉伸应变 | |||
断裂断裂 | 3.5 | % | ISO 527-2 |
Tensile Creep Modulus(1 hr)Tensile Creep Modulus (1 hr) | -- | MPa | ISO 899-1 |
拉伸蠕变模量拉伸蠕变模量 | |||
1000 hr1000 hr | -- | MPa | ISO 899-1 |
弯曲模量Flexural Modulus | 9000 | MPa | ISO 178 |
弯曲强度Flexural Stress | 290 | MPa | ISO 178 |
压缩强度Compressive Stress | 240 | MPa | ISO 604 |
剪切强度Shear Strength | 90.0 | MPa | ASTM D732 |
抗磨损性Abrasion Resistance | 10.0 | mm3 | ISO 4649 |
洛氏硬度洛氏硬度 | |||
M 级M 级 | 101 | ISO 2039-2 | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
密度Density | 1.39 | g/cm3 | ISO 1183 |
收缩率Molding Shrinkage | ISO 294-4 | ||
TDAcross Flow | 1.1 | % | ISO 294-4 |
MDFlow | 0.30 | % | ISO 294-4 |
吸水率吸水率 | |||
饱和,23℃,2.00 mmSaturation,23℃,2.00 mm | 5.7 | % | ISO 62 |
平衡,23℃,50% RH,2.00 mmEquilibrium,23℃,2.00 mm,50% RH | 1.8 | % | ISO 62 |
23℃,24hr23℃,24 hr | 1.2 | % | ISO 62 |
顶出温度Ejection Temperature | 210 | ℃ | |
Specific Heat Capacity of MeltSpecific Heat Capacity of Melt | 2210 | J/kg/℃ | |
Thermal Conductivity of MeltThermal Conductivity of Melt | 0.22 | W/m/K |