产品参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
2.6 |
g/10min |
| 熔体流动速率 |
190℃/2.16kg |
ISO 1133 |
2.6 |
g/10min |
| 单体含量 |
|
Internal Method |
6.5 |
% |
| 物理性能 |
比重 |
|
ASTM D-792 |
0.935 |
g/cm3 |
| 比重 |
|
ISO 1183/A |
0.935 |
g/cm3 |
| 机械性能 |
拉伸屈服强度 |
Compression Molded |
ASTM D-638 |
10 |
MPa |
| 拉伸屈服强度 |
Compression Molded |
ISO 527-2/508 |
10 |
MPa |
| 拉伸断裂强度 |
Compression Molded |
ASTM D-638 |
20.1 |
MPa |
| 拉伸断裂强度 |
Compression Molded |
ISO 527-2/508 |
20.1 |
MPa |
| 拉伸断裂伸长率 |
Compression Molded |
ASTM D-638 |
640 |
% |
| 拉伸断裂伸长率 |
Compression Molded |
ISO 527-2/508 |
640 |
% |
| 薄膜厚度-Tested |
|
|
50.8 |
um |
| 拉伸屈服强度 |
50.8um |
ASTM D-882 |
|
|
| TD |
MD |
|
|
|
| 11.1 |
11.3 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| MPa |
| 拉伸屈服强度 |
50.8um |
ISO 527-3 |
|
| TD |
MD |
| 11.5 |
11.3 |
| MPa |
| 拉伸断裂强度 |
50.8um |
ASTM D-882 |
|
| TD |
MD |
| 31.8 |
31.8 |
| MPa |
| 拉伸断裂强度 |
50.8um |
ISO 527-3 |
|
| TD |
MD |
| 31.8 |
31.8 |
| MPa |
| 拉伸断裂伸长率 |
50.8um |
ASTM D-882 |
|
| MD |
TD |
| 460 |
510 |
| % |
| 拉伸断裂伸长率 |
50.8um |
ISO 527-3 |
|
| MD |
TD |
| 460 |
510 |
| % |
| 落锤冲击 |
50.8um |
ASTM D-1709B |
410 |
g |
| 落锤冲击 |
50.8um |
ISO 7765-1/B |
410 |
g |
| 埃尔曼多夫撕裂强度 |
50.8um |
ASTM D-1922 |
|
| MD |
TD |
| 270 |
390 |
| g |
| 埃尔曼多夫撕裂强度 |
50.8um |
ISO 6383-2 |
|
| MD |
TD |
| 1200 |
1700 |
| N |
| 加工性能 |
熔体温度 |
|
|
193 |
℃ |
| 热性能 |
维卡软化点 |
|
ASTM D-1525 |
88.9 |
℃ |
| 维卡软化点 |
|
ISO 306 |
88.9 |
℃ |
| 熔化温度 |
|
DSC |
103 |
℃ |
| 光学性能 |
光泽度 |
45°，50.8um |
ASTM D-2457 |
76 |
|
| 雾度 |
50.8um |
ASTM D-1003 |
3.7 |
% |
| 雾度 |
50.8um |
ISO 14782 |
3.7 |
% |
EAA简介：乙烯丙烯酸共聚物（Ethylene Acrylic Acid 简称EAA）是一种具有热塑性和极高粘接性的聚合物，由于羧基团的存在以及氢键的作用，聚合物的结晶化被抑制，主链的线性被破坏，因此提高了EAA的透明性和韧性，降低了熔点和软化点。当MI相同时，随着AA含量的增加，EAA的透明性、韧性、粘接性、耐环境应力开裂性会增加；相反，其刚性、湿蒸汽透射率、抗蠕变性、耐化学性会更好。当AA含量相同时，随着MI的增加，EAA的粘接性、加工性会更好；相反，其韧性、耐环境应力开裂性会增加。