MVI

1133

220°C×10KG

ml/10min

27

50°C /hr；1KG

°C

102

Vicat Softening Temp

306

50°C /hr；5KG

°C

95

120°C /hr；1KG

°C

103

120°C /hr；5KG

°C

98

HDT/A

75

1.81MPa, unanneal

°C

80

0.45MPa, unanneal

°C

86

Izod Impact

180/1A

Notched(23°C)

KJ/m²

25

180/1A

Notched(－30°C)

KJ/m²

12

Charpy Impact

179

Notched

KJ/m²

27

Unnotched

KJ/m²

NA

Tensile Strength

527

50mm/min, yield

MPa

42

35

179/2D

50mm/min, break

MPa

Tensile Elongation

527

50mm/min

%

37

Flexural Strength

178

2mm/min

MPa

62

Flexural Modulus

178

2mm/min

GPa

2.05

Ball Indentation Hardness

2039-1

H358/30

─

97

Flammability

─

─

UL-94

1.5mm HB

Mass Density

1183

23°C

g/cm³

1.04

Shrinkage Ratio

─

─

%

0.3~0.6

Linear Thermal Expansion

─

─

×10－⁵/°C

8~10

Coefficient

Product Description

─

─

─

Electro-Plating