牌号简介About
15%玻璃纤维的易流动注射成型等级;适用于刚性、坚固和尺寸稳定的技术零件(例如计时器表盘、拨动开关、旋钮、恒温器零件、烤箱门把手、烤面包机外壳和烤架)。 Ultradur B 4300 G3 is an easy flowing injection molding PBT with 15% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. Applications Typical applications include timer dials, toggles, knobs, parts for thermostats, oven-door handles, toaster housings and grills.
产品描述Product Description
厂家:德国巴斯夫BASF Polyurethanes GmbH
类别:PBTpolybutylene terephthalate
用途:把手;旋钮;外壳;
颜色:可用颜色,黑色,自然色
加工条件:注射成型Injection Molding
性能特点:防火阻燃等级HB; 尺寸稳定性好; 韧性好; 易流动;Good flexibility,Good Dimensional Stability,Good liquidity,HB
填料:玻璃纤维 15
技术参数Technical Data
物理性能
额定值Nominal Value
单位Units
测试方法Test Method
密度Density
1.42
g/cm3
ISO 1183
熔体体积流动速率熔体体积流动速率
250℃,2.16 kg250℃/2.16 kg
15.0
cm3/10min
ISO 1133
吸水率Water Absorption
ISO 62
饱和,23℃Saturation, 73°F
0.40
%
ISO 62
平衡,23℃,50% RHEquilibrium, 73°F, 50% RH
0.20
%
ISO 62
粘数Viscosity Number 33
112
cm3/g
ISO 307
收缩率Mold Shrinkage 44
MD:自由的free, longitudinal
0.50
%
TD:自由的free, transverse
1.4
%
机械性能
额定值Nominal Value
单位Units
测试方法Test Method
拉伸模量Tensile Modulus
6200
MPa
ISO 527-2
拉伸强度拉伸强度
断裂断裂
100
MPa
ISO 527-2
拉伸应变拉伸应变
断裂断裂
3.5
%
ISO 527-2
冲击性能
额定值Nominal Value
单位Units
测试方法Test Method
简支梁缺口冲击强度简支梁缺口冲击强度
23℃23℃
5.5
kJ/m2
ISO 179/1eA
简支梁无缺口冲击强度简支梁无缺口冲击强度
23℃23℃
41
kJ/m2
ISO 179/1eU
热性能
额定值Nominal Value
单位Units
测试方法Test Method
热变形温度Heat Deflection Temperature
0.45 MPa,未退火66 psi, Unannealed
220
℃
ISO 75-2/B
1.8 MPa,未退火264 psi, Unannealed
200
℃
ISO 75-2/A
熔融温度Melting Temperature
223
℃
ISO 11357-3
线性热膨胀系数线性热膨胀系数
MD:23~80℃MD:23 到 80℃
4.0E-5
1/℃
ISO 11359-2
最高使用温度最高使用温度
short cycle operationshort cycle operation
210
℃
电气性能
额定值Nominal Value
单位Units
测试方法Test Method
体积电阻率Volume Resistivity
1.0E 13
ohms·cm
IEC 60093
相对电容率Relative Permittivity
IEC 60250
100 Hz100 Hz
0.00120
IEC 60250
1 MHz1 MHz
0.0150
IEC 60250
耗散因数Dissipation Factor
IEC 60250
100 Hz100 Hz
3.7E-4
IEC 60250
1 MHz1 MHz
3.7E-4
IEC 60250
阻燃性能
额定值Nominal Value
单位Units
测试方法Test Method
阻燃等级Flame Rating
UL 94
0.80 mm0.8 mm
HB
UL 94
1.60 mm1.6 mm
HB
UL 94
Flammability by Electrical Sources of Ignition - Method BH(4.00 mm)Flammability by Electrical Sources of Ignition - Method BH (4.00 mm)
HB
IEC 60707
补充信息
额定值Nominal Value
单位Units
测试方法Test Method
汽车材料汽车材料
1.00 mm 1.00 mm
Pass
FMVSS 302
牌号简介About |
---|
15%玻璃纤维的易流动注射成型等级;适用于刚性、坚固和尺寸稳定的技术零件(例如计时器表盘、拨动开关、旋钮、恒温器零件、烤箱门把手、烤面包机外壳和烤架)。 Ultradur B 4300 G3 is an easy flowing injection molding PBT with 15% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. Applications Typical applications include timer dials, toggles, knobs, parts for thermostats, oven-door handles, toaster housings and grills. |
产品描述Product Description
厂家:德国巴斯夫BASF Polyurethanes GmbH
类别:PBTpolybutylene terephthalate
用途:把手;旋钮;外壳;
颜色:可用颜色,黑色,自然色
加工条件:注射成型Injection Molding
性能特点:防火阻燃等级HB; 尺寸稳定性好; 韧性好; 易流动;Good flexibility,Good Dimensional Stability,Good liquidity,HB
填料:玻璃纤维 15
技术参数Technical Data | |||
---|---|---|---|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
密度Density | 1.42 | g/cm3 | ISO 1183 |
熔体体积流动速率熔体体积流动速率 | |||
250℃,2.16 kg250℃/2.16 kg | 15.0 | cm3/10min | ISO 1133 |
吸水率Water Absorption | ISO 62 | ||
饱和,23℃Saturation, 73°F | 0.40 | % | ISO 62 |
平衡,23℃,50% RHEquilibrium, 73°F, 50% RH | 0.20 | % | ISO 62 |
粘数Viscosity Number 33 | 112 | cm3/g | ISO 307 |
收缩率Mold Shrinkage 44 | |||
MD:自由的free, longitudinal | 0.50 | % | |
TD:自由的free, transverse | 1.4 | % | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
拉伸模量Tensile Modulus | 6200 | MPa | ISO 527-2 |
拉伸强度拉伸强度 | |||
断裂断裂 | 100 | MPa | ISO 527-2 |
拉伸应变拉伸应变 | |||
断裂断裂 | 3.5 | % | ISO 527-2 |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
简支梁缺口冲击强度简支梁缺口冲击强度 | |||
23℃23℃ | 5.5 | kJ/m2 | ISO 179/1eA |
简支梁无缺口冲击强度简支梁无缺口冲击强度 | |||
23℃23℃ | 41 | kJ/m2 | ISO 179/1eU |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
热变形温度Heat Deflection Temperature | |||
0.45 MPa,未退火66 psi, Unannealed | 220 | ℃ | ISO 75-2/B |
1.8 MPa,未退火264 psi, Unannealed | 200 | ℃ | ISO 75-2/A |
熔融温度Melting Temperature | 223 | ℃ | ISO 11357-3 |
线性热膨胀系数线性热膨胀系数 | |||
MD:23~80℃MD:23 到 80℃ | 4.0E-5 | 1/℃ | ISO 11359-2 |
最高使用温度最高使用温度 | |||
short cycle operationshort cycle operation | 210 | ℃ | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
体积电阻率Volume Resistivity | 1.0E 13 | ohms·cm | IEC 60093 |
相对电容率Relative Permittivity | IEC 60250 | ||
100 Hz100 Hz | 0.00120 | IEC 60250 | |
1 MHz1 MHz | 0.0150 | IEC 60250 | |
耗散因数Dissipation Factor | IEC 60250 | ||
100 Hz100 Hz | 3.7E-4 | IEC 60250 | |
1 MHz1 MHz | 3.7E-4 | IEC 60250 | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
阻燃等级Flame Rating | UL 94 | ||
0.80 mm0.8 mm | HB | UL 94 | |
1.60 mm1.6 mm | HB | UL 94 | |
Flammability by Electrical Sources of Ignition - Method BH(4.00 mm)Flammability by Electrical Sources of Ignition - Method BH (4.00 mm) | HB | IEC 60707 | |
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
汽车材料汽车材料 | |||
1.00 mm 1.00 mm | Pass | FMVSS 302 |