Vydyne? R530H BK08

聚酰胺66

30% 玻璃纤维增强材料

Ascend Performance Materials Operations LLC

产品说明：

Vydyne R530H BK08 is high-flow, heat-stabilized, 30% glass-fiber reinforced PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved machine feed and flow.

Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.

Vydyne R530H BK08 is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R530H BK08 has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.

Typical Applications/End Uses:
To come

填料/增强材料	玻璃纤维增强材料, 30% 填料按重量
添加剂	热稳定剂润滑剂
特性	出色的外观抗冻抗溶剂性流动性高耐化学性良好耐疲劳性能耐汽油性热稳定性润滑
用途	汽车的发动机罩下的零件
机构评级	ASTM D 4066 PA0121G30 ASTM D 6779 PA0121G30
UL文件号	E70062
外观	黑色
形式	粒子
加工方法	注射成型

物理性能	干燥	调节后的	单位制	测试方法
密度	1.37	--	g/cm3	ISO 1183
收缩率				ISO 294-4
垂直流动方向 : 23°C, 2.00 mm	0.90	--	%	ISO 294-4
流动方向 : 23°C, 2.00 mm	0.40	--	%	ISO 294-4
吸水率				ISO 62
23°C, 24 hr	0.90	--	%	ISO 62
平衡, 50% RH	1.9	--	%	ISO 62

机械性能	干燥	调节后的	单位制	测试方法
拉伸模量(23°C)	10000	7400	MPa	ISO 527-2
拉伸应力(断裂, 23°C)	195	135	MPa	ISO 527-2
拉伸应变(断裂, 23°C)	3.0	5.0	%	ISO 527-2
弯曲模量(23°C)	9600	6000	MPa	ISO 178
弯曲应力(23°C)	270	190	MPa	ISO 178
Poisson's Ratio(23°C)	0.40	--		ISO 527

冲击性能	干燥	调节后的	单位制	测试方法
简支梁缺口冲击强度				ISO 179
-30°C	10	11	kJ/m2	ISO 179
23°C	11	13	kJ/m2	ISO 179
简支梁无缺口冲击强度				ISO 179
-30°C	65	80	kJ/m2	ISO 179
23°C	75	85	kJ/m2	ISO 179
悬壁梁缺口冲击强度				ISO 180
-30°C	10	11	kJ/m2	ISO 180
23°C	12	13	kJ/m2	ISO 180

热性能	干燥	调节后的	单位制	测试方法
热变形温度
0.45 MPa, 未退火	260	--	°C	ISO 75-2/B
1.8 MPa, 未退火	250	--	°C	ISO 75-2/A
熔融温度	260	--	°C	ISO 11357-3
线形热膨胀系数				ISO 11359-2
流动 : 23 到 55°C, 2.00 mm	2.2E-5	--	cm/cm/°C	ISO 11359-2
横向 : 23 到 55°C, 2.00 mm	1.1E-4	--	cm/cm/°C	ISO 11359-2
RTI Elec				UL 746
0.750 mm	140	--	°C	UL 746
1.50 mm	140	--	°C	UL 746
3.00 mm	140	--	°C	UL 746
RTI Imp				UL 746
0.750 mm	120	--	°C	UL 746
1.50 mm	120	--	°C	UL 746
3.00 mm	120	--	°C	UL 746
RTI				UL 746
0.750 mm	125	--	°C	UL 746
1.50 mm	140	--	°C	UL 746
3.00 mm	140	--	°C	UL 746

电气性能	干燥	调节后的	单位制	测试方法
体积电阻率(3.00 mm)	1.0E+13	--	ohms·cm	IEC 60093
介电强度(1.00 mm)	20	--	kV/mm	IEC 60243
耐电弧性(3.00 mm)	PLC 6	--		ASTM D495
漏电起痕指数(3.00 mm)	250 到 399	--	V	IEC 60112
高电弧燃烧指数(HAI)				UL 746
0.750 mm	PLC 0	--		UL 746
1.50 mm	PLC 0	--		UL 746
3.00 mm	PLC 0	--		UL 746
高电压电弧起痕速率 (HVTR)	PLC 1	--		UL 746
热丝引燃 (HWI)				UL 746
0.750 mm	PLC 4	--		UL 746
1.50 mm	PLC 3	--		UL 746
3.00 mm	PLC 4	--		UL 746

可燃性	干燥	调节后的	单位制	测试方法
UL 阻燃等级				UL 94
0.750 mm	HB	--		UL 94
1.50 mm	HB	--		UL 94
3.00 mm	HB	--		UL 94
灼热丝易燃指数				IEC 60695-2-12
0.750 mm	675	--	°C	IEC 60695-2-12
1.50 mm	675	--	°C	IEC 60695-2-12
3.00 mm	675	--	°C	IEC 60695-2-12
热灯丝点火温度				IEC 60695-2-13
0.750 mm	700	--	°C	IEC 60695-2-13
1.50 mm	700	--	°C	IEC 60695-2-13
3.00 mm	700	--	°C	IEC 60695-2-13

注射	干燥	单位制
干燥温度	80.0	°C
干燥时间	4.0	hr
建议的最大回制料比例	25	%
料筒后部温度	280 到 310	°C
料筒中部温度	280 到 310	°C
料筒前部温度	280 到 310	°C
射嘴温度	280 到 310	°C
加工（熔体）温度	285 到 305	°C
模具温度	65.0 到 95.0	°C