Technical Data Sheet
Petrothene LR686001
WC Polyolefin Compound
Product Description
Petrothene LR686001 is selected by customers for use as insulation for foam/skin telephone singles, and is a natural, expandable, high density polyethylene compound containing a chemical blowing agent. LR686001 is highly stabilized to ensure OIT retention and thermal stability during processing, oven aging, and in pedestal testing. This product contains a processing aid and a metal deactivator to prevent degradation from copper while the cable is in service.
Petrothene LR686001 meets the requirements of the following: ASTM D 1248, Type III, Class A, Category 4, Grade E9; Federal LP390C, Type II, Class H, Category 4, Grade 1; REA PE-89.
Regulatory Status
For regulatory compliance information, see Petrothene LR686001 Product Stewardship Bulletin (PSB) andSafety Data Sheet (SDS).
Status Commercial:Active
Availability NorthAmerica
Application Wire Cable
Market Wire Cable ProcessingMethod Wire Cable
Typical PropertiesNominalValueEnglish UnitsNominalValueSIUnits TestMethod
Physical |
|||||
Melt Flow Rate, (190 °C/2.16 kg) |
0.80 |
g/10 min |
0.80 |
g/10 min |
ASTM D1238 |
Density, (23 °C) |
0.948 |
g/cm3 |
0.948 |
g/cm3 |
ASTM D1505 |
Mechanical |
|||||
Tensile Stress at Break |
3600 |
psi |
24.8 |
MPa |
ASTM D638 |
Tensile Stress at Yield |
3000 |
psi |
20.7 |
MPa |
ASTM D638 |
Tensile Elongation at Break |
800 |
% |
800 |
% |
ASTM D638 |
Thermal |
|||||
Low Temperature Brittleness, Fco |
-105 |
°F |
-76 |
°C |
ASTM D746 |
Electrical |
|||||
Volume Resistivity |
1 x 102o |
ohm*cm |
1 x 102o |
ohm*cm |
ASTM D257 |
Dielectric Constant, 1 MHz |
2.35 |
2.35 |
ASTM D150 |
||
Dissipation Factor, 1 MHz |
0.00026 |
0.00026 |
ASTM D150 |
高密度聚乙烯(High Density Polyethylene,简称为“HDPE”)又称低压聚乙烯,是一种结晶度高、非极性面呈一定程度的半透明状。PE具有优良的耐大多数生活和工业用化学品的特性。
【基本特性】
高密度聚乙烯是一种不透明白色腊状材料,比重比水轻,比重为0.941~0.960,柔软而且有韧性,但比LDPE略硬,也略能伸长,无味。
【燃烧特性】
易燃,离火后能继续燃烧,火焰上端呈黄色,下端呈蓝色,燃烧时会熔融,有液体滴落,无黑烟冒出,同时,发出石蜡燃烧时发出的气味。
【主要优点】
耐有机溶剂,电绝缘性优良,低温时,仍能保持一定的韧性。表面硬度,拉伸强度,刚性等机械强度都高于LDPE,接近于PP,比PP韧,但表面光洁度不如PP。
【主要缺点】
机械性能差,透气差,易变形,易老化,易发脆,脆性低于PP,易应力开裂,表面硬度低,易刮伤。难印刷,印刷时,需进行表面放电处理,不能电镀,表面无光泽。
【应用场合】
用于挤出包装薄膜,绳索,编织袋,渔网,水管;注塑低档日用品及外壳,非承载荷构件,胶箱,周转箱;挤出吹塑容器,中空制品,瓶子。
用途:电话绝缘 、电线电缆应用
特性备注:热稳定性好生产厂商:利安德巴塞尔
HDPE利安德巴塞尔LR686001 英文名称:Polyethylene(简称PE)
用途:聚乙烯可加工制成薄膜、电线电缆护套、管材、纤维等。广泛用于农业、电子电气、机械、日用杂品等方面
比重: 0.91-0.96克/立方厘米成型收缩率:1.5-3.6% 成型温度:140-220
特点:耐腐蚀性,电绝缘性(尤其高频绝缘性),可以氯化,化学交联、辐照交联改性,可用玻璃纤维增强。低压聚乙烯的熔点、刚性、硬度和强度较高,吸水性小,有良好的电性能和耐辐射性;高压聚乙烯的柔软性,伸长率,冲击强度和渗透性较好;超高分子量聚乙烯冲击强度高,耐疲劳,. 低压聚 乙烯适于制作耐腐蚀零件和绝缘零件;高压聚乙烯适于制作薄膜等;超高分子量聚乙烯适于制作减震,及传动零件。
干燥:如果存储恰当则无须干燥。
熔化温度:220260C。对于分子较大的材料,建议熔化温度范围在200250C之间。
模具温度:5095C。6mm以下壁厚的塑件应使用较高的模具温度,6mm 以上壁厚的塑件使用较低的模具温度。塑件冷却温度应当均匀以减小收缩率的差异。加工周期时间,冷却腔道直径应不小于8mm,并且距模具表面的距离应在1.3d 之内(这里“d”是冷却腔道的直径)。
注射压力:7001050bar。
注射速度:建议使用高速注射。
流道和浇口:流道直径在4到7.5mm之间,流道长度应尽可能短。可以使用各种类型的浇口,浇口长度不要超过0.75mm。特别适用于使用热流道模具。
典型用途:食品容器、存储容器、家用厨具、密封盖、管材等。