Lexan PC EXL9330物性
-60℃延展性,紫外稳定.耐燃性V-0/5VA. 非卤化,不含溴.
Property
| TYPICAL PROPERTIES(1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
590
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
620
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
130
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
21400
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
900
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
21000
|
kgf/cm2
|
ASTM D 790
|
|
|
Tensile Stress, yield, 50 mm/min
|
55
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
60
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
6
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
125
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2100
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
85
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2200
|
MPa
|
ISO 178
|
|
|
Hardness, H358/30
|
90
|
MPa
|
ISO 2039-1
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
81
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
69
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -50°C
|
59
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, 23°C, 6.4mm
|
65
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, double-gated, 23°C
|
108
|
cm-kgf/cm
|
SABIC Method
|
|
|
Instrumented Impact Total Energy, 23°C
|
539
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, unnotched 80*10*3 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, notched 80*10*3 +23°C
|
70
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*3 -30°C
|
55
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 63.5*12.7*3.2, 23°C
|
80
|
kJ/m2
|
ISO 180/4A
|
|
|
Izod Impact, notched 63.5*12.7*3.2, -30°C
|
65
|
kJ/m2
|
ISO 180/4A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
75
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
60
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
142
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
134
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
120
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
124
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
6.66E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
6.66E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, 23°C to 80°C, flow
|
7.2E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, 23°C to 80°C, xflow
|
7.7E-05
|
1/°C
|
ISO 11359-2
|
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/50
|
140
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
142
|
°C
|
ISO 306
|
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
135
|
°C
|
ISO 75/Be
|
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
124
|
°C
|
ISO 75/Ae
|
|
|
Relative Temp Index, Elec
|
125
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
115
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
120
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.18
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm
|
0.4 - 0.8
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm
|
0.4 - 0.8
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
10
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.19
|
g/cm2
|
ISO 1183
|
|
|
Water Absorption, (23°C/sat)
|
0.35
|
%
|
ISO 62
|
|
|
Moisture Absorption (23°C / 50% RH)
|
0.15
|
%
|
ISO 62
|
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
9
|
cm210 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Dielectric Strength, in oil, 3.2 mm
|
17
|
kV/mm
|
ASTM D 149
|
|
|
Relative Permittivity, 50/60 Hz
|
2.95
|
-
|
ASTM D 150
|
|
|
Relative Permittivity, 1 MHz
|
2.9
|
-
|
ASTM D 150
|
|
|
Dissipation Factor, 50/60 Hz
|
0.0024
|
-
|
ASTM D 150
|
|
|
Dissipation Factor, 1 MHz
|
0.0085
|
-
|
ASTM D 150
|
|
|
Hot Wire Ignition {PLC)
|
1
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
|
Volume Resistivity
|
1.E+15
|
Ohm-cm
|
IEC 60093
|
|
|
Surface Resistivity, ROA
|
1.E+15
|
Ohm
|
IEC 60093
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
16
|
kV/mm
|
IEC 60243-1
|
|
|
Relative Permittivity, 50/60 Hz
|
2.6
|
-
|
IEC 60250
|
|
|
Relative Permittivity, 1 MHz
|
2.7
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 50/60 Hz
|
0.001
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 1 MHz
|
0.008
|
-
|
IEC 60250
|
|
|
Comparative Tracking Index
|
225
|
V
|
IEC 60112
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
1.49
|
mm
|
UL 94
|
|
|
UL Recognized, 94-5VA Rating (3)
|
2.99
|
mm
|
UL 94
|
|
|
Glow Wire Flammability Index 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
|
Glow Wire Ignitability Temperature, 1.0 mm
|
825
|
°C
|
IEC 60695-2-13
|
|
|
Oxygen Index (LOI)
|
35
|
%
|
ISO 4589
|
|
UV-light, water exposure/immersion |
F1
|
-
|
UL 746C
|
|