1300S 日本旭化成PA66
产品描述Product Description
厂家：日本旭化成Asahi Kasei Corporation
类别：PA66PA66
用途：汽车领域的应用;连接器;消费品应用领域;配件;
性能特点：机械强度好; 易流动; 韧性好;Good Rigidity,Good flexibility,Good liquidity
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | 1.14 | g/cm3 | ASTM D792 |
| 收缩率Molding Shrinkage | |||
| MD：2.0 mmMD2.0mm | 1.3 | % | ASTM D995 |
| TD：2.0 mmTD2.0mm | 2.0 | % | ASTM D995 |
| 吸水率Water Absorption | |||
| 23℃，24hr(23°C, 24 hr) | 2.5 | % | ASTM D570 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Heat Deflection Temperature | |||
| 0.45 MPa，未退火0.45MPa 未退火 | 230 | ℃ | ASTM D648 |
| 1.8 MPa，未退火1.80MPa 未退火 | 70 | ℃ | ASTM D648 |
| 导热系数Thermal Conductivity | 0.2 | W/m/K | JIS R2618 |
| 线性热膨胀系数线膨胀系数 | |||
| 比热Specific Heat | 1670 | J/Kg/℃ | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 绝缘强度绝缘强度 | |||
| 20 | KV/mm | ASTM D149 | |
| 耗散因数Dissipation Factor | |||
| 相比漏电起痕指数相对漏电起痕指数 | 600 | V | ASTM D3638 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级防火等级 | |||
| 0.40mm | V-2 | UL 94 | |
| 0.71mm | V-2 | UL 94 | |
| 1.50mm | V-2 | UL 94 | |
| 3.00mm | V-2 | UL 94 | |
| 极限氧指数氧指数 | 26 | % | ASTM D2863 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃23°C | 39 | J/m | ASTM D256 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度Rockwell Hardness | 80 | M 级 | ASTM D785 |
| 洛氏硬度Rockwell Hardness | 120 | R 级 | ASTM D785 |
| 拉伸强度拉伸强度 | |||
| 23℃23°C | 79 | MPa | ASTM D638 |
| 拉伸应变Tensile Elongation at Break | |||
| 断裂，23℃23°C | 50 | % | ASTM D638 |
| 弯曲强度Flexural Strength | |||
| 23℃23°C | 118 | MPa | ASTM D790 |
| 弯曲模量Flexural Modulus | |||
| 23℃23°C | 2800 | MPa | ASTM D790 |