长期供应台湾奇美ABS PA-709
POLYLAC? PA-709是一种丙烯腈丁二烯苯乙烯(ABS)产品。特性包括: 阻燃/额定火焰 通过 ROHS 认证 耐冲击
| 技术参数Technical Data | |||
|---|---|---|---|
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 密度Specific Gravity | |||
| ---- 33 | 1.03 | g/cm3 | ASTM D792 |
| 23℃23°C | 1.03 | g/cm3 | ISO 1183 |
| 熔体质量流动速率熔体质量流动速率 | |||
| 200℃，5.0kg200℃/5.0 kg | 0.50 | g/10min | ASTM D1238 |
| 熔体体积流动速率熔体体积流动速率 | |||
| 220℃，10 kg220℃/10.0 kg | 5.00 | cm3/10min | ISO 1133 |
| 收缩率Molding Shrinkage | 0.40 到 0.70 | % | ISO 294-4 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 简支梁缺口冲击强度Charpy Notched Impact Strength | ISO 179 | ||
| -30℃-30°C | 29 | kJ/m2 | ISO 179 |
| 23℃23°C | 42 | kJ/m2 | ISO 179 |
| 悬臂梁缺口冲击强度Notched Izod Impact Strength | |||
| 23℃，3.2mm23°C, 3.20 mm | 450 | J/m | ASTM D256 |
| 23℃，6.4mm23°C, 6.40 mm | 370 | J/m | ASTM D256 |
| -30℃-30°C | 27 | kJ/m2 | ISO 180-1A |
| 23℃23°C | 40 | kJ/m2 | ISO 180-1A |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 热变形温度Deflection Temperature Under Load | |||
| 1.8 MPa，未退火264 psi, Unannealed | 85.0 | ℃ | ASTM D648 |
| 1.8 MPa，未退火264 psi, Unannealed | 82.0 | ℃ | ISO 75-2/A |
| 1.8 MPa，退火264 psi, Annealed | 95.0 | ℃ | ASTM D648 |
| 1.8 MPa，退火264 psi, Annealed | 98.0 | ℃ | ISO 75-2/A |
| 维卡软化温度Vicat Softening Temperature | |||
| A50-- | 105 | ℃ | ASTM D1525，ISO 306 |
| B50-- | 97.0 | ℃ | ISO 306 |
| 线性热膨胀系数线性热膨胀系数 | |||
| MDMD | 9.3E-5 | 1/℃ | ISO 11359-2 |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 阻燃等级1.5 mm | |||
| 1.50 mm | HB | UL 94 | |
|
|
额定值Nominal Value | 单位Units | 测试方法Test Method |
| 洛氏硬度洛氏硬度 | |||
| R 级R 级 | 102 | ASTM D785 | |
| 拉伸强度Tensile Strength | |||
| 屈服屈服 44 | 39.1 | MPa | ASTM D638 |
| 屈服Yield | 40.0 | MPa | ISO 527-2/50 |
| 断裂Break | 31.0 | MPa | ISO 527-2/50 |
| 拉伸应变Tensile Elongation | |||
| 断裂Break 44 | 40 | % | ASTM D638 |
| 断裂Break | 35 | % | ISO 527-2/50 |
| 弯曲模量Flexural Modulus | |||
| ---- 55 | 2210 | MPa | ASTM D790 |
| ---- 66 | 1800 | MPa | ISO 178 |
| 弯曲强度Flexural Strength | |||
| ---- 55 | 62.5 | MPa | ASTM D790 |
| ---- 66 | 58.0 | MPa | ISO 178 |
POLYLAC? PA-704LRP
POLYLAC? PA-707
POLYLAC? PA-709
POLYLAC? PA-709H
POLYLAC? PA-709P
POLYLAC? PA-709S
POLYLAC? PA-716
POLYLAC? PA-717C
POLYLAC? PA-726
POLYLAC? PA-726M
POLYLAC? PA-727
POLYLAC? PA-737 A03
POLYLAC? PA-737
POLYLAC? PA-737T
POLYLAC? PA-746M
POLYLAC? PA-747
POLYLAC? PA-747F
POLYLAC? PA-747H
POLYLAC? PA-747R
POLYLAC? PA-747S A01
POLYLAC? PA-747S
POLYLAC? PA-749
POLYLAC? PA-749S
POLYLAC? PA-756
POLYLAC? PA-756H
POLYLAC? PA-756S
POLYLAC? PA-757 A01
POLYLAC? PA-757 AB
POLYLAC? PA-757 J01
POLYLAC? PA-757
POLYLAC? PA-757F
POLYLAC? PA-757G J08
POLYLAC? PA-757H J01
POLYLAC? PA-757H
POLYLAC? PA-757N
POLYLAC? PA-763
POLYLAC? PA-764
POLYLAC? PA-764B